PC LEXAN™ HFD4413-BK1E711 SABIC INNOVATIVE NANSHA

231

Unit Price:US$ 2,950 /MT
Packaging Specification:
25 KG/PKG
Packaging Material:
Paper bag
Supply Quantity:
29.7MT
Delivery Terms:
FOB
Port of Loading :
Guangzhou port, China
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View

serv********View

+86 ********View

For more details, please contact the supplier!

Material Description

Material Properties:High mobility｜Hydrolysis resistance
Application Areas:Electrical applications｜Automotive Applications｜Mechanical accessories
Color:--
Grade:--

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result	Test Unit
Impact strength of simply supported beam without notch	23°C	ISO 179/1eU	40	kJ/m²
Suspended wall beam without notch impact strength	23°C	ASTM D4812	850	J/m
	Suspended wall beam without notch impact strength	-30°C7	ISO 180/1U	30	kJ/m²
	Suspended wall beam without notch impact strength	Suspended wall beam without notch impact strength	23°C7	ISO 180/1U	37	kJ/m²
Dart impact	23°C,TotalEnergy	ASTM D3763	17.0	J
Impact strength of simply supported beam without notch	-30°C	ISO 179/1eU	49	kJ/m²
Charpy Notched Impact Strength	23°C	ISO 179/1eA	12	kJ/m²
Charpy Notched Impact Strength	Charpy Notched Impact Strength	-30°C	ISO 179/1eA	11	kJ/m²
flammability	Test Condition	Test Method	Test Result	Test Unit
Hot filament ignition temperature	1.0mm	IEC 60695-2-13	850	°C
Burning wire flammability index	2.0mm	IEC 60695-2-12	960	°C
UL flame retardant rating	0.8mm	UL 94	HB
UL flame retardant rating	UL flame retardant rating	0.30mm	UL 94	HB
mechanical properties	Test Condition	Test Method	Test Result	Test Unit
tensile strength	Yield4	ASTM D638	111	Mpa
Tensile modulus		ASTM D638	7870	Mpa
bending strength	Yield,50.0mmSpan	ASTM D790	182	Mpa
Bending modulus	50.0mmSpan	ASTM D790	7760	Mpa
elongation	Break	ISO 527-2/5	2.1	%
	elongation	Yield	ISO 527-2/5	2.5	%
	elongation	elongation	Yield4	ASTM D638	3.0	%
tensile strength	Break	ISO 527-2/5	125	Mpa
	tensile strength	Break4	ASTM D638	111	Mpa
	tensile strength	tensile strength	Yield	ISO 527-2/5	115	Mpa
thermal performance	Test Condition	Test Method	Test Result	Test Unit
RTI		UL 746	80.0	°C
Hot deformation temperature	0.45MPa,Unannealed,3.20mm	ASTM D648	130	°C
	Hot deformation temperature	1.8MPa,Unannealed,3.20mm	ASTM D648	125	°C
	Hot deformation temperature	Hot deformation temperature	1.8MPa,Unannealed,64.0mmSpan8	ISO 75-2/Af	129	°C
Vicat softening temperature		ISO 306/B120	143	°C
Ball Pressure Test	125°C	IEC 60695-10-2	通过
Linear coefficient of thermal expansion	MD:-40to40°C	ASTME831	3E-05	cm/cm/°C
	Linear coefficient of thermal expansion	MD:23to80°C	ISO 11359-2	3E-05	cm/cm/°C
		Linear coefficient of thermal expansion	TD:-40to40°C	ASTME831	7E-05	cm/cm/°C
		Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	TD:23to80°C	ISO 11359-2	7E-05	cm/cm/°C
RTI Elec		UL 746	80.0	°C
RTI Imp		UL 746	80.0	°C
Physical properties	Test Condition	Test Method	Test Result	Test Unit
Water absorption rate	Equilibrium,23°C,50%RH	ISO 62	0.12	%
Water absorption rate	Water absorption rate	Saturation,23°C	ISO 62	0.30	%
Shrinkage rate	TD:3.20mm	Internal Method	0.10-0.30	%
Shrinkage rate	Shrinkage rate	MD:3.20mm	Internal Method	0.10-0.30	%
Melt Volume Flow Rate (MVR)	300°C/1.2kg	ISO 1133	18.0	cm3/10min
melt mass-flow rate	300°C/1.2kg	ASTM D1238	16	g/10min

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.

Supplier Join

Get App

Top

PC LEXAN™ HFD4413-BK1E711 SABIC INNOVATIVE NANSHA

Material Description

Technical Data Sheet

Sourcing & Prices

Selling & Verification

Explore Materials

Price Index