Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PC HFD4413-BK1E711 SABIC INNOVATIVE NANSHA
LEXAN™
Electrical applications、Automotive Applications、Mechanical accessories
High mobility、Hydrolysis resistance
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | SABIC INNOVATIVE NANSHA/HFD4413-BK1E711 |
|---|---|---|---|
| Charpy Notched Impact Strength | 23°C | ISO 179/1eA | 12 kJ/m² |
| Suspended wall beam without notch impact strength | -30°C7 | ISO 180/1U | 30 kJ/m² |
| Dart impact | 23°C,TotalEnergy | ASTM D3763 | 17.0 J |
| Charpy Notched Impact Strength | -30°C | ISO 179/1eA | 11 kJ/m² |
| Suspended wall beam without notch impact strength | 23°C | ASTM D4812 | 850 J/m |
| Impact strength of simply supported beam without notch | 23°C | ISO 179/1eU | 40 kJ/m² |
| Suspended wall beam without notch impact strength | 23°C7 | ISO 180/1U | 37 kJ/m² |
| Impact strength of simply supported beam without notch | -30°C | ISO 179/1eU | 49 kJ/m² |
| Mechanical properties | Test Condition | Test Method | SABIC INNOVATIVE NANSHA/HFD4413-BK1E711 |
|---|---|---|---|
| tensile strength | 屈服 | ISO 527-2/5 | 115 Mpa |
| 断裂 | ISO 527-2/5 | 125 Mpa | |
| Tensile modulus | ASTM D638 | 7870 Mpa | |
| tensile strength | 屈服4 | ASTM D638 | 111 Mpa |
| bending strength | 屈服,50.0mm跨距 | ASTM D790 | 182 Mpa |
| elongation | 屈服4 | ASTM D638 | 3.0 % |
| tensile strength | 断裂4 | ASTM D638 | 111 Mpa |
| elongation | 屈服 | ISO 527-2/5 | 2.5 % |
| 断裂 | ISO 527-2/5 | 2.1 % | |
| Flexural modulus | 50.0mm跨距 | ASTM D790 | 7760 Mpa |
| flammability | Test Condition | Test Method | SABIC INNOVATIVE NANSHA/HFD4413-BK1E711 |
|---|---|---|---|
| Hot filament ignition temperature | 1.0mm | IEC 60695-2-13 | 850 °C |
| UL flame retardant rating | 0.8mm | UL 94 | HB |
| Burning wire flammability index | 2.0mm | IEC 60695-2-12 | 960 °C |
| UL flame retardant rating | 0.30mm | UL 94 | HB |
| physical property | Test Condition | Test Method | SABIC INNOVATIVE NANSHA/HFD4413-BK1E711 |
|---|---|---|---|
| Shrinkage rate | MD:3.20mm | 内部方法 | 0.10-0.30 % |
| Melt volume flow rate | 300°C/1.2kg | ISO 1133 | 18.0 cm3/10min |
| Water absorption rate | 平衡,23°C,50%RH | ISO 62 | 0.12 % |
| 饱和,23°C | ISO 62 | 0.30 % | |
| Shrinkage rate | TD:3.20mm | 内部方法 | 0.10-0.30 % |
| melt mass-flow rate | 300°C/1.2kg | ASTM D1238 | 16 g/10min |
| Thermal performance | Test Condition | Test Method | SABIC INNOVATIVE NANSHA/HFD4413-BK1E711 |
|---|---|---|---|
| Linear coefficient of thermal expansion | TD:23到80°C | ISO 11359-2 | 7E-05 cm/cm/°C |
| vicat | ISO 306/B120 | 143 °C | |
| Linear coefficient of thermal expansion | TD:-40到40°C | ASTME831 | 7E-05 cm/cm/°C |
| Heat distortion temperature | 0.45MPa,未退火,3.20mm，HDT | ASTM D648 | 130 °C |
| Linear coefficient of thermal expansion | MD:23到80°C | ISO 11359-2 | 3E-05 cm/cm/°C |
| Heat distortion temperature | 1.8MPa,未退火,64.0mm跨距8，HDT | ISO 75-2/Af | 129 °C |
| RTI Imp | UL 746 | 80.0 °C | |
| RTI | UL 746 | 80.0 °C | |
| Heat distortion temperature | 1.8MPa,未退火,3.20mm，HDT | ASTM D648 | 125 °C |
| ball-indentation hardness | 125°C | IEC 60695-10-2 | 通过 |
| Linear coefficient of thermal expansion | MD:-40到40°C | ASTME831 | 3E-05 cm/cm/°C |
| RTI Elec | UL 746 | 80.0 °C |