PA66 LNP™ LUBRICOMP™ RF-1004 SABIC INNOVATIVE US
166
- Unit Price:US$ 3,272 /MT
- Packaging Specification:25 KG/PKG
- Packaging Material:Paper bag
- Supply Quantity:20MT
- Delivery Terms:FOB
- Port of Loading :China Main Port
- Accepted Payment Methods:T/T
- Shipping:Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 ********View
serv********View
For more details, please contact the supplier!
Material Description
- Material Properties:Thermal stability｜High temperature resistance｜high strength｜Filler: Glass fiber reinforced material｜20% filler by weight
- Application Areas:Automotive components｜Electronic and electrical components
- Color:--
- Grade:Extrusion grade
Technical Data Sheet
Compare
| thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Heat Deflection Temperature | 0.45MPa,未退火,3.20mm | ASTM D648 | 260 °C |
| 1.8MPa,未退火,3.20mm | ASTM D648 | 247 °C | |
| 1.8MPa,未退火,64.0mm跨距 | ISO 75-2/Af | 221 °C | |
| Linear coefficient of thermal expansion | MD：-40到40°C | ASTME831 | 3.8E-05 cm/cm/°C |
| MD：-40到40°C | ISO 11359-2 | 3.9E-05 cm/cm/°C | |
| TD：-40到40°C | ASTME831 | 7.9E-05 cm/cm/°C | |
| TD：-40到40°C | ISO 11359-2 | 7.9E-05 cm/cm/°C |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Impact strength of cantilever beam gap | 23°C | ISO 180/1A | 8.6 kJ/m² |
| Suspended wall beam without notch impact strength | 23°C | ISO 180/1U | 56 kJ/m² |
| Dart impact | 23°C,EnergyatPeakLoad | ASTM D3763 | 11.4 J |
| Multi axis Instrumented Impact Energy | ISO 6603-2 | 2.49 J |
| Physical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| shrinkage rate | MD：24小时 | ASTM D955 | 0.50 % |
| TD：24hr | ASTM D955 | 1.2 % | |
| TD:24小时 | ISO 294-4 | 1.2 % | |
| MD:24小时 | ISO 294-4 | 0.47 % | |
| Water absorption rate | 24hr,50%RH | ASTM D570 | 0.80 % |
| mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| tensile strength | 断裂 | ISO 527-2 | 160 Mpa |
| elongation | 断裂 | ASTM D638 | 3.6 % |
| Tensile strain | 断裂 | ISO 527-2 | 3.7 % |
| flexural modulus | ASTM D790 | 5860 Mpa | |
| ISO 178 | 7000 Mpa | ||
| bending strength | ASTM D790 | 231 Mpa | |
| ISO 178 | 242 Mpa | ||
| coefficient of friction | Dynamic | ASTM D3702Modified | 0.68 |
| Static | ASTM D3702Modified | 0.52 | |
| Wear factor | Washer | ASTM D3702Modified | 80.0 10^-10in^5-min/ft-lb-hr |
| Tensile modulus | ASTM D638 | 7170 Mpa | |
| ISO 527-2/1 | 7300 Mpa | ||
| tensile strength | 断裂 | ASTM D638 | 157 Mpa |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.