Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PA66 RF-1004 SABIC INNOVATIVE US
LNP™ LUBRICOMP™
Automotive components,Electronic and electrical components
Thermal stability,High temperature resistan,high strength,Filler: Glass fiber reinf,20% filler by weight
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | SABIC INNOVATIVE US/RF-1004 |
|---|---|---|---|
| Suspended wall beam without notch impact strength | 23°C | ISO 180/1U | 56 kJ/m² |
| Multi axis Instrumented Impact Energy | ISO 6603-2 | 2.49 J | |
| Impact strength of cantilever beam gap | 23°C | ISO 180/1A | 8.6 kJ/m² |
| Dart impact | 23°C,EnergyatPeakLoad | ASTM D3763 | 11.4 J |
| Mechanical properties | Test Condition | Test Method | SABIC INNOVATIVE US/RF-1004 |
|---|---|---|---|
| Tensile modulus | ISO 527-2/1 | 7300 Mpa | |
| bending strength | ASTM D790 | 231 Mpa | |
| tensile strength | 断裂 | ISO 527-2 | 160 Mpa |
| Wear factor | Washer | ASTM D3702Modified | 80.0 10^-10in^5-min/ft-lb-hr |
| tensile strength | 断裂 | ASTM D638 | 157 Mpa |
| Flexural modulus | ASTM D790 | 5860 Mpa | |
| Tensile modulus | ASTM D638 | 7170 Mpa | |
| elongation | 断裂 | ASTM D638 | 3.6 % |
| bending strength | ISO 178 | 242 Mpa | |
| coefficient of friction | Static | ASTM D3702Modified | 0.52 |
| Tensile strain | 断裂 | ISO 527-2 | 3.7 % |
| Flexural modulus | ISO 178 | 7000 Mpa | |
| coefficient of friction | Dynamic | ASTM D3702Modified | 0.68 |
| physical property | Test Condition | Test Method | SABIC INNOVATIVE US/RF-1004 |
|---|---|---|---|
| Shrinkage rate | MD:24小时 | ISO 294-4 | 0.47 % |
| MD：24小时 | ASTM D955 | 0.50 % | |
| Water absorption rate | 24hr,50%RH | ASTM D570 | 0.80 % |
| Shrinkage rate | TD：24hr | ASTM D955 | 1.2 % |
| TD:24小时 | ISO 294-4 | 1.2 % |
| Thermal performance | Test Condition | Test Method | SABIC INNOVATIVE US/RF-1004 |
|---|---|---|---|
| Linear coefficient of thermal expansion | TD：-40到40°C | ASTME831 | 7.9E-05 cm/cm/°C |
| TD：-40到40°C | ISO 11359-2 | 7.9E-05 cm/cm/°C | |
| Heat distortion temperature | 0.45MPa,未退火,3.20mm，HDT | ASTM D648 | 260 °C |
| Linear coefficient of thermal expansion | MD：-40到40°C | ASTME831 | 3.8E-05 cm/cm/°C |
| MD：-40到40°C | ISO 11359-2 | 3.9E-05 cm/cm/°C | |
| Heat distortion temperature | 1.8MPa,未退火,64.0mm跨距，HDT | ISO 75-2/Af | 221 °C |
| 1.8MPa,未退火,3.20mm，HDT | ASTM D648 | 247 °C |