PC LEXAN™  FXD1414T BL4E059X SABIC INNOVATIVE SHANGHAI

190
  • Unit Price:US$ 5,259 /MT
  • Packaging Specification:
    25 KG/PKG
  • Packaging Material:
    Paper bag
  • Supply Quantity:
    10MT
  • Delivery Terms:
    FOB
  • Port of Loading :
    China Main Port
  • Accepted Payment Methods:
    T/T
  • Shipping:
    Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View
serv********View

For more details, please contact the supplier!

Material Description

  • Material Properties:Low temperature resistance｜transparent｜Easy to process｜Middle flow
  • Application Areas:Household appliances｜Bottle cap｜Electronic field｜Electrical field
  • Color:--
  • Grade:Injection grade

Material Certification

UL

Technical Data Sheet

impact performanceTest ConditionTest MethodTest Result
Charpy Notched Impact Strength-30°CISO 179/1eA60 kJ/m²
Charpy Notched Impact Strength23°CISO 179/1eA70 kJ/m²
Impact strength of simply supported beam without notch-30°CISO 179/1eU无断裂
Impact strength of simply supported beam without notch23°CISO 179/1eU无断裂
Suspended wall beam without notch impact strength-30°CISO 180/1U无断裂
Suspended wall beam without notch impact strength23°CISO 180/1U无断裂
Dart impact23°C, Total EnergyASTM D376376.0 J
mechanical propertiesTest ConditionTest MethodTest Result
Tensile modulus--3ASTM D6382240 Mpa
Tensile modulus--ISO 527-2/12300 Mpa
tensile strengthYield4ASTM D63859.0 Mpa
tensile strengthYieldISO 527-2/5057.0 Mpa
tensile strengthBreak4ASTM D63851.0 Mpa
tensile strengthBreakISO 527-2/5054.0 Mpa
elongationYield4ASTM D6385.8 %
elongationYieldISO 527-2/505.4 %
elongationBreak4ASTM D63884 %
elongationBreakISO 527-2/50110 %
Bending modulus50.0 mm Span5ASTM D7902220 Mpa
Bending modulus--6ISO 1782150 Mpa
bending strength--6,7ISO 17889.0 Mpa
bending strengthYield, 50.0 mm Span5ASTM D79085.0 Mpa
injectionTest ConditionTest MethodTest Result
drying temperature120 °C
drying time3.0 to 4.0 hr
Suggested maximum moisture content0.020 %
Suggested injection volume40 to 60 %
Temperature at the rear of the barrel215 to 295 °C
Temperature in the middle of the barrel280 to 305 °C
Temperature at the front of the material cylinder295 to 315 °C
Spray nozzle temperature290 to 310 °C
Processing (melt) temperature295 to 315 °C
Mold temperature70 to 95 °C
Back pressure0.300 to 0.700 Mpa
Screw speed40 to 70 rpm
Exhaust hole depth0.025 to 0.076 mm
thermal performanceTest ConditionTest MethodTest Result
Hot deformation temperature1.8 MPa, Unannealed, 3.20 mmASTM D648122 °C
Hot deformation temperature1.8 MPa, Unannealed, 4.00 mm, 64.0 mm Span10ISO 75-2/Af116 °C
Vicat softening temperature--ASTM D152511138 °C
Vicat softening temperature--ISO 306/B120142 °C
Ball Pressure Test123 to 127°CIEC 60695-10-2通过
Linear coefficient of thermal expansionFlow : -40 to 95°CASTM E8316.7E-5 cm/cm/°C
Linear coefficient of thermal expansionFlow : 23 to 80°CISO 11359-26.7E-5 cm/cm/°C
Linear coefficient of thermal expansionAcross Flow : -40 to 95°CASTM E8318.0E-5 cm/cm/°C
Linear coefficient of thermal expansionAcross Flow : 23 to 80°CISO 11359-28.0E-5 cm/cm/°C
Physical propertiesTest ConditionTest MethodTest Result
melt mass-flow rate300°C/1.2 kgASTM D123810 g/10 min
Melt Volume Flow Rate (MVR)300°C/1.2 kgISO 11339.00 cm3/10min
Shrinkage rateFlow 2Internal Method0.40 - 0.80 %
Shrinkage rateFlow : 3.20 mmInternal Method0.40 - 0.80 %
Shrinkage rateAcross FlowFlow : 3.20 mmInternal Method0.40 - 0.80 %
Water absorption rateSaturation, 23°CISO 620.12 %
Water absorption rateEquilibrium, 23°C, 50% RHISO 620.090 %
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.