Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PC FXD1414T BL4E059X SABIC INNOVATIVE SHANGHAI
LEXAN™
Household appliances、Bottle cap、Electronic field、Electrical field
Low temperature resistanc、transparent、Easy to process、Middle flow
UL
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | SABIC INNOVATIVE SHANGHAI/FXD1414T BL4E059X |
|---|---|---|---|
| Charpy Notched Impact Strength | 23°C | ISO 179/1eA | 70 kJ/m² |
| Impact strength of simply supported beam without notch | -30°C | ISO 179/1eU | 无断裂 |
| Charpy Notched Impact Strength | -30°C | ISO 179/1eA | 60 kJ/m² |
| Impact strength of simply supported beam without notch | 23°C | ISO 179/1eU | 无断裂 |
| Suspended wall beam without notch impact strength | 23°C | ISO 180/1U | 无断裂 |
| Dart impact | 23°C, Total Energy | ASTM D3763 | 76.0 J |
| Suspended wall beam without notch impact strength | -30°C | ISO 180/1U | 无断裂 |
| Mechanical properties | Test Condition | Test Method | SABIC INNOVATIVE SHANGHAI/FXD1414T BL4E059X |
|---|---|---|---|
| tensile strength | 屈服4 | ASTM D638 | 59.0 Mpa |
| elongation | 断裂4 | ASTM D638 | 84 % |
| Tensile modulus | --3 | ASTM D638 | 2240 Mpa |
| Flexural modulus | 50.0 mm 跨距5 | ASTM D790 | 2220 Mpa |
| elongation | 断裂 | ISO 527-2/50 | 110 % |
| bending strength | --6,7 | ISO 178 | 89.0 Mpa |
| Flexural modulus | --6 | ISO 178 | 2150 Mpa |
| bending strength | 屈服, 50.0 mm 跨距5 | ASTM D790 | 85.0 Mpa |
| tensile strength | 断裂 | ISO 527-2/50 | 54.0 Mpa |
| 屈服 | ISO 527-2/50 | 57.0 Mpa | |
| elongation | 屈服 | ISO 527-2/50 | 5.4 % |
| 屈服4 | ASTM D638 | 5.8 % | |
| tensile strength | 断裂4 | ASTM D638 | 51.0 Mpa |
| Tensile modulus | -- | ISO 527-2/1 | 2300 Mpa |
| physical property | Test Condition | Test Method | SABIC INNOVATIVE SHANGHAI/FXD1414T BL4E059X |
|---|---|---|---|
| Water absorption rate | 平衡, 23°C, 50% RH | ISO 62 | 0.090 % |
| Shrinkage rate | 流动 2 | 内部方法 | 0.40 - 0.80 % |
| 横向流动 : 3.20 mm | 内部方法 | 0.40 - 0.80 % | |
| Melt volume flow rate | 300°C/1.2 kg | ISO 1133 | 9.00 cm3/10min |
| melt mass-flow rate | 300°C/1.2 kg | ASTM D1238 | 10 g/10 min |
| Shrinkage rate | 流动 : 3.20 mm | 内部方法 | 0.40 - 0.80 % |
| Water absorption rate | 饱和, 23°C | ISO 62 | 0.12 % |
| Thermal performance | Test Condition | Test Method | SABIC INNOVATIVE SHANGHAI/FXD1414T BL4E059X |
|---|---|---|---|
| vicat | -- | ASTM D152511 | 138 °C |
| -- | ISO 306/B120 | 142 °C | |
| Linear coefficient of thermal expansion | 流动 : -40 到 95°C | ASTM E831 | 6.7E-5 cm/cm/°C |
| 横向 : 23 到 80°C | ISO 11359-2 | 8.0E-5 cm/cm/°C | |
| 流动 : 23 到 80°C | ISO 11359-2 | 6.7E-5 cm/cm/°C | |
| ball-indentation hardness | 123 到 127°C | IEC 60695-10-2 | 通过 |
| Linear coefficient of thermal expansion | 横向 : -40 到 95°C | ASTM E831 | 8.0E-5 cm/cm/°C |
| Heat distortion temperature | 1.8 MPa, 未退火, 3.20 mm，HDT | ASTM D648 | 122 °C |
| 1.8 MPa, 未退火, 4.00 mm, 64.0 mm 跨距10，HDT | ISO 75-2/Af | 116 °C |
| injection | Test Condition | Test Method | SABIC INNOVATIVE SHANGHAI/FXD1414T BL4E059X |
|---|---|---|---|
| screw speed | 40 to 70 rpm | ||
| Suggested maximum moisture content | 0.020 % | ||
| Processing (melt) temperature | 295 to 315 °C | ||
| drying temperature | 120 °C | ||
| Suggested injection volume | 40 to 60 % | ||
| drying time | 3.0 to 4.0 hr | ||
| Temperature in the middle of the barrel | 280 to 305 °C | ||
| Temperature at the rear of the barrel | 215 to 295 °C | ||
| Exhaust hole depth | 0.025 to 0.076 mm | ||
| Temperature at the front of the material cylinder | 295 to 315 °C | ||
| Back pressure | 0.300 to 0.700 Mpa | ||
| Temperature | 70 to 95 °C | ||
| Spray nozzle temperature | 290 to 310 °C |