EAA PRIMACOR™ 5980I DOW USA
474
- Unit Price:US$ 9,769 /MT
- Packaging Specification:25 KG/PKG
- Packaging Material:Paper bag
- Supply Quantity:30MT
- Delivery Terms:FOB
- Port of Loading :China Main Port
- Accepted Payment Methods:T/T
- Shipping:Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 ********View
serv********View
For more details, please contact the supplier!
Material Description
- Material Properties:High gloss
- Application Areas:Power tools
- Color:--
- Grade:Hot melt grade
Technical Data Sheet
| hardness | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Shore hardness | ShoreD | ASTMD2240 | 50 |
| thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Vicat softening temperature | ASTMD1525 | 42.2 °C | |
| Melting temperature | Internal Method | 77.2 °C | |
| Vicat softening temperature | ASTM D-1525 | 42.2 ℃ | |
| ISO 306 | 42.2 ℃ | ||
| Melting temperature | Internal Method | 77.2 ℃ |
| Basic Performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| melt mass-flow rate | 190℃/2.16kg | ISO 1133 | 300 g/10min |
| Monomer content | Internal Method | 20.5 % | |
| melt mass-flow rate | 190℃/2.16kg | ASTM D-1238 | 300 g/10min |
| Physical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| melt mass-flow rate | 125°C/2.16kg2 | ASTMD1238 | 14 g/10min |
| 190°C/2.16kg3 | ASTMD1238 | 300 g/10min | |
| Content of comonomer | Internal Method | 20.5 % |
| mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Tensile modulus | Compression Molded，2%Secant | ASTMD638 | 33.1 Mpa |
| tensile strength | Break,Compression Molded | ASTMD638 | 9.65 Mpa |
| elongation | Break,Compression Molded | ASTMD638 | 390 % |
| Tensile modulus | Compression Molded，2% Secant | ASTM D-638 | 33.1 MPa |
| Compression Molded，2% Secant | ISO 527-2 | 33.1 MPa | |
| tensile strength | Compression Molded，Break | ASTM D-638 | 9.65 MPa |
| Compression Molded，Break | ISO 527-2 | 9.65 MPa | |
| Elongation at Break | Compression Molded | ASTM D-638 | 390 % |
| Compression Molded | ISO 527-2 | 390 % |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.