EAA 5980I DOW USA
PRIMACOR™
Power tools
High gloss
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| hardness | Test Condition | Test Method | DOW USA/5980I |
|---|---|---|---|
| 邵氏D | ASTMD2240,ISO868 | 50 |
| Basic performance | Test Condition | Test Method | DOW USA/5980I |
|---|---|---|---|
| melt mass-flow rate | 190℃/2.16kg | ISO 1133 | 300 g/10min |
| Monomer content | % | Internal Method 20.5 | |
| melt mass-flow rate | 190℃/2.16kg | ASTM D-1238 | 300 g/10min |
| Mechanical properties | Test Condition | Test Method | DOW USA/5980I |
|---|---|---|---|
| elongation | 断裂,模压成型 | ASTMD638,ISO527-2 | 390 % |
| tensile breaking strength | Compression Molded | ISO 527-2 | 9.65 MPa |
| tensile strength | 断裂,模压成型 | ASTMD638,ISO527-2 | 9.65 Mpa |
| tensile breaking strength | Compression Molded | ASTM D-638 | 9.65 MPa |
| tensile elongation at break | Compression Molded | ASTM D-638 | 390 % |
| Tensile modulus -2% secant | 模压成型 | ASTMD638,ISO527-2 | 33.1 Mpa |
| Tensile modulus -2% Secant | Compression Molded | ISO 527-2 | 33.1 MPa |
| tensile elongation at break | Compression Molded | ISO 527-2 | 390 % |
| Tensile modulus -2% Secant | Compression Molded | ASTM D-638 | 33.1 MPa |
| physical property | Test Condition | Test Method | DOW USA/5980I |
|---|---|---|---|
| melt mass-flow rate | 190°C/2.16kg3 | ASTMD1238,ISO1133 | 300 g/10min |
| 125°C/2.16kg2 | ASTMD1238,ISO1133 | 14 g/10min | |
| Content of comonomer 4 | 内部方法 | 20.5 % |
| Thermal performance | Test Condition | Test Method | DOW USA/5980I |
|---|---|---|---|
| vicat | ASTM D-1525 | 42.2 ℃ | |
| ISO 306 | 42.2 ℃ | ||
| ASTMD1525,ISO306 | 42.2 °C | ||
| 内部方法 | 77.2 °C | ||
| melting temperature | ℃ | Internal Method 77.2 |