PC LEXAN™ EXL401-799 SABIC INNOVATIVE US
126
- Unit Price:US$ 5,159 /MT
- Packaging Specification:25 KG/PKG
- Packaging Material:Paper bag
- Supply Quantity:15MT
- Delivery Terms:FOB
- Port of Loading :China Main Port
- Accepted Payment Methods:T/T
- Shipping:Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 ********View
serv********View
For more details, please contact the supplier!
Material Description
- Material Properties:High mobility｜Ductility at low temperature｜Short molding cycle
- Application Areas:Electronic and Electrical Applications｜Aerospace Applications｜lens
- Color:--
- Grade:Injection grade
Technical Data Sheet
Compare
| physical property | Test Condition | Test Method | Test Result |
|---|---|---|---|
| melt mass-flow rate | ASTM D1238 | 7.5 g/10min | |
| Melt volume flow rate | ISO 1133 | 6.50 cm3/10min | |
| Shrinkage rate | 内部方法 | 0.20-0.60 % | |
| 内部方法 | 0.20-0.60 % | ||
| Water absorption rate | ISO 62 | 0.15 % | |
| ISO 62 | 0.40 % |
| flammability | Test Condition | Test Method | Test Result |
|---|---|---|---|
| UL flame retardant rating | UL 94 | HB |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Suspended wall beam without notch impact strength | ISO 180/1U | NoBreak | |
| ISO 180/1U | NoBreak | ||
| Dart impact | ASTM D3763 | 40.0 J | |
| Charpy Notched Impact Strength | ISO 179/1eA | 15 kJ/m² | |
| ISO 179/1eA | 25 kJ/m² | ||
| Impact strength of simply supported beam without notch | ISO 179/1eU | NoBreak | |
| ISO 179/1eU | NoBreak | ||
| Impact strength of cantilever beam gap | ISO 180/1A | 10 kJ/m² | |
| ISO 180/1A | 25 kJ/m² |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Tensile modulus | ASTM D638 | 3950 Mpa | |
| ISO 527-2/1 | 3900 Mpa | ||
| bending strength | ISO 178 | 98.0 Mpa | |
| ASTM D790 | 103 Mpa | ||
| tensile strength | ASTM D638 | 55.0 Mpa | |
| ISO 527-2/5 | 54.0 Mpa | ||
| ASTM D638 | 45.0 Mpa | ||
| ISO 527-2/5 | 48.0 Mpa | ||
| elongation | ASTM D638 | 4.3 % | |
| Tensile strain | ISO 527-2/5 | 4.3 % | |
| elongation | ASTM D638 | 14 % | |
| Tensile strain | ISO 527-2/5 | 8.7 % | |
| Flexural modulus | ASTM D790 | 3500 Mpa | |
| ISO 178 | 3450 Mpa |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Heat distortion temperature | ASTM D648 | 137 °C | |
| ISO 75-2/Ae | 135 °C | ||
| vicat | ASTM D152510 | 146 °C | |
| ISO 306/B50 | 146 °C | ||
| ISO 306/B120 | 146 °C | ||
| ball-indentation hardness | IEC 60695-10-2 | Pass | |
| Linear coefficient of thermal expansion | ASTME831 | 4.7E-05 cm/cm/°C | |
| ISO 11359-2 | 4.7E-05 cm/cm/°C | ||
| ASTME831 | 7E-05 cm/cm/°C | ||
| ISO 11359-2 | 7E-05 cm/cm/°C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.