Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PC EXL401-799 SABIC INNOVATIVE US
LEXAN™
Electronic and Electrical、Aerospace Applications、lens
High mobility、Ductility at low temperat、Short molding cycle
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | SABIC INNOVATIVE US/EXL401-799 |
|---|---|---|---|
| Charpy Notched Impact Strength | 23°C | ISO 179/1eA | 25 kJ/m² |
| Dart impact | 23°C,TotalEnergy | ASTM D3763 | 40.0 J |
| Impact strength of simply supported beam without notch | -30°C | ISO 179/1eU | NoBreak |
| Charpy Notched Impact Strength | -30°C | ISO 179/1eA | 15 kJ/m² |
| Impact strength of simply supported beam without notch | 23°C | ISO 179/1eU | NoBreak |
| Impact strength of cantilever beam gap | -30°C | ISO 180/1A | 10 kJ/m² |
| Suspended wall beam without notch impact strength | 23°C | ISO 180/1U | NoBreak |
| Impact strength of cantilever beam gap | 23°C | ISO 180/1A | 25 kJ/m² |
| Suspended wall beam without notch impact strength | -30°C | ISO 180/1U | NoBreak |
| Mechanical properties | Test Condition | Test Method | SABIC INNOVATIVE US/EXL401-799 |
|---|---|---|---|
| Tensile modulus | ISO 527-2/1 | 3900 Mpa | |
| tensile strength | 断裂 | ISO 527-2/5 | 48.0 Mpa |
| elongation | 屈服 | ASTM D638 | 4.3 % |
| Tensile strain | 屈服 | ISO 527-2/5 | 4.3 % |
| tensile strength | 断裂 | ASTM D638 | 45.0 Mpa |
| Flexural modulus | 50.0mm跨距 | ASTM D790 | 3500 Mpa |
| tensile strength | 屈服 | ISO 527-2/5 | 54.0 Mpa |
| Tensile modulus | ASTM D638 | 3950 Mpa | |
| bending strength | 屈服,50.0mm跨距 | ASTM D790 | 103 Mpa |
| elongation | 断裂 | ASTM D638 | 14 % |
| bending strength | ISO 178 | 98.0 Mpa | |
| Flexural modulus | ISO 178 | 3450 Mpa | |
| Tensile strain | 断裂 | ISO 527-2/5 | 8.7 % |
| tensile strength | 屈服 | ASTM D638 | 55.0 Mpa |
| flammability | Test Condition | Test Method | SABIC INNOVATIVE US/EXL401-799 |
|---|---|---|---|
| UL flame retardant rating | 0.75mm | UL 94 | HB |
| physical property | Test Condition | Test Method | SABIC INNOVATIVE US/EXL401-799 |
|---|---|---|---|
| Shrinkage rate | MD：3.20mm | 内部方法 | 0.20-0.60 % |
| Melt volume flow rate | 300°C/1.2kg | ISO 1133 | 6.50 cm3/10min |
| Shrinkage rate | TD：3.20mm | 内部方法 | 0.20-0.60 % |
| Water absorption rate | 平衡,23°C,50%RH | ISO 62 | 0.40 % |
| 饱和,23°C | ISO 62 | 0.15 % | |
| melt mass-flow rate | 300°C/1.2kg | ASTM D1238 | 7.5 g/10min |
| Thermal performance | Test Condition | Test Method | SABIC INNOVATIVE US/EXL401-799 |
|---|---|---|---|
| vicat | -- | ISO 306/B120 | 146 °C |
| Linear coefficient of thermal expansion | TD：-40到40°C | ASTME831 | 7E-05 cm/cm/°C |
| TD：-40到40°C | ISO 11359-2 | 7E-05 cm/cm/°C | |
| ball-indentation hardness | 75°C | IEC 60695-10-2 | Pass |
| vicat | -- | ISO 306/B50 | 146 °C |
| Linear coefficient of thermal expansion | MD：-40到40°C | ASTME831 | 4.7E-05 cm/cm/°C |
| MD：-40到40°C | ISO 11359-2 | 4.7E-05 cm/cm/°C | |
| vicat | ASTM D152510 | 146 °C | |
| Heat distortion temperature | 1.8MPa,Unannealed,100mmSpan，HDT | ISO 75-2/Ae | 135 °C |
| 1.8MPa,未退火,3.20mm，HDT | ASTM D648 | 137 °C |