PBT VALOX™ VIC4311 BK1066L SABIC INNOVATIVE US
179
- Unit Price:US$ 3,517 /MT
- Packaging Specification:25 KG/PKG
- Packaging Material:Paper bag
- Supply Quantity:20MT
- Delivery Terms:FOB
- Port of Loading :China Main Port
- Accepted Payment Methods:T/T
- Shipping:Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 ********View
serv********View
For more details, please contact the supplier!
Material Description
- Material Properties:Glass fiber reinforced
- Application Areas:Engine hood parts｜Plastic bag｜Automotive External Parts｜Electronic field｜Electrical field
- Color:--
- Grade:Injection grade
Technical Data Sheet
Compare
| thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Heat Deflection Temperature | 0.45MPa,未退火,3.20mm | ASTM D648 | 220 °C |
| 1.8MPa,未退火,3.20mm | ASTM D648 | 205 °C | |
| 1.8MPa,Unannealed,64.0mmSpan | ISO 75-2/Af | 175 °C | |
| vicat | ASTM D152510 | 180 °C | |
| -- | ISO 306/B50 | 175 °C | |
| -- | ISO 306/B120 | 170 °C | |
| ball-indentation hardness | 75°C | IEC 60695-10-2 | Pass |
| Linear coefficient of thermal expansion | MD：-40to40°C | ASTME831 | 2.3E-05 cm/cm/°C |
| MD：-30到30°C | ASTME831 | 3E-05 cm/cm/°C | |
| MD：-40到40°C | ISO 11359-2 | 2.3E-05 cm/cm/°C | |
| TD：-40到40°C | ASTME831 | 1.1E-04 cm/cm/°C | |
| TD：-40到40°C | ISO 11359-2 | 1.1E-04 cm/cm/°C |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Charpy Notched Impact Strength | 23°C | ISO 179/1eA | 16 kJ/m² |
| Impact strength of cantilever beam gap | -30°C | ISO 180/1A | 9.9 kJ/m² |
| 23°C | ISO 180/1A | 13 kJ/m² | |
| Dart impact | 23°C,TotalEnergy | ASTM D3763 | 13.9 J |
| Physical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| melt mass-flow rate | 250°C/5.0kg | ASTM D1238 | 19 g/10min |
| Melt volume flow rate | 250°C/5.0kg | ISO 1133 | 15.6 cm3/10min |
| shrinkage rate | MD：3.20mm | 内部方法 | 0.20-0.40 % |
| MD：6.40mm | 内部方法 | 0.60-0.80 % | |
| TD：3.20mm | 内部方法 | 0.60-0.80 % | |
| Water absorption rate | 饱和,23°C | ISO 62 | 0.090 % |
| 平衡,23°C,50%RH | ISO 62 | 0.070 % |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Surface Resistivity | ASTM D257 | 1E+16 ohms | |
| dielectric constant | 50Hz | ASTM D150 | 3.00 |
| 60Hz | ASTM D150 | 3.00 |
| mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Tensile modulus | ASTM D638 | 8370 Mpa | |
| ISO 527-2/1 | 7380 Mpa | ||
| tensile strength | 屈服 | ASTM D638 | 83.0 Mpa |
| 屈服 | ISO 527-2/5 | 86.5 Mpa | |
| 断裂 | ASTM D638 | 84.0 Mpa | |
| 断裂 | ISO 527-2/5 | 84.0 Mpa | |
| elongation | 屈服 | ASTM D638 | 3.0 % |
| Tensile strain | 屈服 | ISO 527-2/5 | 3.0 % |
| elongation | 断裂 | ASTM D638 | 4.0 % |
| Tensile strain | 断裂 | ISO 527-2/5 | 4.0 % |
| flexural modulus | 50.0mm跨距 | ASTM D790 | 6080 Mpa |
| ISO 178 | 6190 Mpa | ||
| bending strength | ISO 178 | 139 Mpa | |
| 屈服,50.0mm跨距 | ASTM D790 | 129 Mpa |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.