Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PBT VIC4311 BK1066L SABIC INNOVATIVE US
VALOX™
Engine hood parts,Plastic bag,Automotive External Parts,Electronic field,Electrical field
Glass fiber reinforced
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | SABIC INNOVATIVE US/VIC4311 BK1066L |
|---|---|---|---|
| Charpy Notched Impact Strength | 23°C | ISO 179/1eA | 16 kJ/m² |
| Dart impact | 23°C,TotalEnergy | ASTM D3763 | 13.9 J |
| Impact strength of cantilever beam gap | -30°C | ISO 180/1A | 9.9 kJ/m² |
| 23°C | ISO 180/1A | 13 kJ/m² |
| thermal performance | Test Condition | Test Method | SABIC INNOVATIVE US/VIC4311 BK1066L |
|---|---|---|---|
| Linear coefficient of thermal expansion | MD：-40to40°C | ASTME831 | 2.3E-05 cm/cm/°C |
| TD：-40到40°C | ASTME831 | 1.1E-04 cm/cm/°C | |
| MD：-30到30°C | ASTME831 | 3E-05 cm/cm/°C | |
| ball-indentation hardness | 75°C | IEC 60695-10-2 | Pass |
| Linear coefficient of thermal expansion | TD：-40到40°C | ISO 11359-2 | 1.1E-04 cm/cm/°C |
| vicat | -- | ISO 306/B120 | 170 °C |
| Heat Deflection Temperature | 0.45MPa,未退火,3.20mm，HDT | ASTM D648 | 220 °C |
| 1.8MPa,未退火,3.20mm，HDT | ASTM D648 | 205 °C | |
| vicat | -- | ISO 306/B50 | 175 °C |
| Heat Deflection Temperature | 1.8MPa,Unannealed,64.0mmSpan，HDT | ISO 75-2/Af | 175 °C |
| Linear coefficient of thermal expansion | MD：-40到40°C | ISO 11359-2 | 2.3E-05 cm/cm/°C |
| vicat | ASTM D152510 | 180 °C |
| mechanical properties | Test Condition | Test Method | SABIC INNOVATIVE US/VIC4311 BK1066L |
|---|---|---|---|
| Tensile strain | 断裂 | ISO 527-2/5 | 4.0 % |
| tensile strength | 断裂 | ISO 527-2/5 | 84.0 Mpa |
| Tensile modulus | ASTM D638 | 8370 Mpa | |
| elongation | 断裂 | ASTM D638 | 4.0 % |
| flexural modulus | 50.0mm跨距 | ASTM D790 | 6080 Mpa |
| tensile strength | 屈服 | ASTM D638 | 83.0 Mpa |
| bending strength | ISO 178 | 139 Mpa | |
| tensile strength | 屈服 | ISO 527-2/5 | 86.5 Mpa |
| Tensile modulus | ISO 527-2/1 | 7380 Mpa | |
| Tensile strain | 屈服 | ISO 527-2/5 | 3.0 % |
| elongation | 屈服 | ASTM D638 | 3.0 % |
| tensile strength | 断裂 | ASTM D638 | 84.0 Mpa |
| bending strength | 屈服,50.0mm跨距 | ASTM D790 | 129 Mpa |
| flexural modulus | ISO 178 | 6190 Mpa |
| Electrical performance | Test Condition | Test Method | SABIC INNOVATIVE US/VIC4311 BK1066L |
|---|---|---|---|
| dielectric constant | 60Hz | ASTM D150 | 3.00 |
| 50Hz | ASTM D150 | 3.00 | |
| Surface Resistivity | ASTM D257 | 1E+16 ohms |
| Physical properties | Test Condition | Test Method | SABIC INNOVATIVE US/VIC4311 BK1066L |
|---|---|---|---|
| shrinkage rate | TD：3.20mm | 内部方法 | 0.60-0.80 % |
| Melt volume flow rate | 250°C/5.0kg | ISO 1133 | 15.6 cm3/10min |
| shrinkage rate | MD：6.40mm | 内部方法 | 0.60-0.80 % |
| Water absorption rate | 饱和,23°C | ISO 62 | 0.090 % |
| 平衡,23°C,50%RH | ISO 62 | 0.070 % | |
| melt mass-flow rate | 250°C/5.0kg | ASTM D1238 | 19 g/10min |
| shrinkage rate | MD：3.20mm | 内部方法 | 0.20-0.40 % |