PA6T Zytel® FR52G30BL DUPONT USA
303
- Unit Price:US$ 8,651 /MT
- Packaging Specification:25 KG/PKG
- Packaging Material:Paper bag
- Supply Quantity:20MT
- Delivery Terms:FOB
- Port of Loading :China Main Port
- Accepted Payment Methods:T/T
- Shipping:Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 ********View
serv********View
For more details, please contact the supplier!
Material Description
- Material Properties:Glass fiber reinforced｜Flame retardant｜Lubricity｜Filler: Glass fiber reinforced material｜30% filler by weight
- Application Areas:Electrical field｜Electronic field｜Electrical appliances｜Automotive sector
- Color:--
- Grade:Injection grade
Technical Data Sheet
Compare
| physical property | Test Condition | Test Method | Test Result |
|---|---|---|---|
| density | ISO 1183 | 1.62 g/cm³ | |
| Shrinkage rate | ISO 294-4 | 0.80 % | |
| ISO 294-4 | 0.30 % |
| flammability | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Limiting Oxygen Index | ISO 4589-2 | 42 % | |
| FMVSS flammability | FMVSS302 | DNI | |
| atomization | ISO 6452 | 95 % | |
| UL flame retardant rating | UL 94 | V-0 | |
| UL 94 | V-0 | ||
| IEC 60695-11-10,-20 | V-0 | ||
| IEC 60695-11-10,-20 | V-0 |
| Supplementary Information | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Odor | VDA270 | 4.50 |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Tensile modulus | ISO 527-2 | 12000 Mpa | |
| tensile strength | ISO 527-2 | 170 Mpa | |
| Tensile strain | ISO 527-2 | 2.0 % | |
| Flexural modulus | ISO 178 | 10500 Mpa | |
| bending strength | ISO 178 | 250 Mpa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | 11 kJ/m² | |
| ISO 179/1eA | 11 kJ/m² | ||
| Impact strength of simply supported beam without notch | ISO 179/1eU | 40 kJ/m² | |
| ISO 179/1eU | 50 kJ/m² | ||
| ISO 179/1eU | 50 kJ/m² |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Volume resistivity | IEC 60093 | >1.0E+15 ohms·cm | |
| dielectric strength | IEC 60243-1 | 34 KV/mm | |
| relative permittivity | IEC 60250 | 3.50 | |
| IEC 60250 | 3.30 | ||
| Dissipation Factor | IEC 60250 | 5E-03 | |
| IEC 60250 | 0.014 | ||
| Compared to the Leakage Tracking Index (CTI) | UL 746 | PLC 1 | |
| IEC 60112 | PLC 1 | ||
| IEC 60112 | PLC 3 |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| melting temperature | ISO 11357-3 | 310 °C | |
| Linear coefficient of thermal expansion | ISO 11359-2 | 2E-05 cm/cm/°C | |
| ISO 11359-2 | 2E-05 cm/cm/°C | ||
| ISO 11359-2 | 1E-05 cm/cm/°C | ||
| ISO 11359-2 | 6.3E-05 cm/cm/°C | ||
| ISO 11359-2 | 5.7E-05 cm/cm/°C | ||
| ISO 11359-2 | 1E-04 cm/cm/°C | ||
| Heat distortion temperature | ISO 75-2/B | 300 °C | |
| ISO 75-2/A | 282 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.