Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PA6T FR52G30BL DUPONT USA
Zytel®
Electrical field、Electronic field、Electrical appliances、Automotive sector
Glass fiber reinforced、Flame retardant、Lubricity、Filler: Glass fiber reinf、30% filler by weight
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | DUPONT USA/FR52G30BL |
|---|---|---|---|
| Charpy Notched Impact Strength | 23°C | ISO 179/1eA | 11 kJ/m² |
| Impact strength of simply supported beam without notch | -40°C | ISO 179/1eU | 40 kJ/m² |
| Charpy Notched Impact Strength | -30°C | ISO 179/1eA | 11 kJ/m² |
| Impact strength of simply supported beam without notch | 23°C | ISO 179/1eU | 50 kJ/m² |
| -30°C | ISO 179/1eU | 50 kJ/m² |
| Supplementary Information | Test Condition | Test Method | DUPONT USA/FR52G30BL |
|---|---|---|---|
| Odor | VDA270 | 4.50 |
| Electrical performance | Test Condition | Test Method | DUPONT USA/FR52G30BL |
|---|---|---|---|
| dielectric strength | IEC 60243-1 | 34 KV/mm | |
| Volume resistivity | IEC 60093 | >1.0E+15 ohms·cm | |
| relative permittivity | 100Hz | IEC 60250 | 3.50 |
| Dissipation Factor | 100Hz | IEC 60250 | 5E-03 |
| relative permittivity | 1MHz | IEC 60250 | 3.30 |
| Compared to the Leakage Tracking Index (CTI) | CTI | UL 746 | PLC 1 |
| 解决方案B | IEC 60112 | PLC 3 | |
| Dissipation Factor | 1MHz | IEC 60250 | 0.014 |
| Compared to the Leakage Tracking Index (CTI) | -- | IEC 60112 | PLC 1 |
| Mechanical properties | Test Condition | Test Method | DUPONT USA/FR52G30BL |
|---|---|---|---|
| Tensile modulus | ISO 527-2 | 12000 Mpa | |
| bending strength | ISO 178 | 250 Mpa | |
| Tensile strain | 断裂 | ISO 527-2 | 2.0 % |
| Flexural modulus | ISO 178 | 10500 Mpa | |
| tensile strength | 断裂 | ISO 527-2 | 170 Mpa |
| flammability | Test Condition | Test Method | DUPONT USA/FR52G30BL |
|---|---|---|---|
| UL flame retardant rating | 3.0mm | IEC 60695-11-10,-20 | V-0 |
| atomization | refraction，F值 | ISO 6452 | 95 % |
| UL flame retardant rating | 3.0mm | UL 94 | V-0 |
| 1.5mm | IEC 60695-11-10,-20 | V-0 | |
| FMVSS flammability | FMVSS302 | DNI | |
| Limiting Oxygen Index | ISO 4589-2 | 42 % | |
| UL flame retardant rating | 1.5mm | UL 94 | V-0 |
| physical property | Test Condition | Test Method | DUPONT USA/FR52G30BL |
|---|---|---|---|
| Shrinkage rate | TD | ISO 294-4 | 0.80 % |
| MD | ISO 294-4 | 0.30 % | |
| density | ISO 1183 | 1.62 g/cm³ |
| Thermal performance | Test Condition | Test Method | DUPONT USA/FR52G30BL |
|---|---|---|---|
| melting temperature | ISO 11357-3 | 310 °C | |
| Linear coefficient of thermal expansion | MD：55to160°C | ISO 11359-2 | 1E-05 cm/cm/°C |
| TD：-- | ISO 11359-2 | 6.3E-05 cm/cm/°C | |
| MD：-40to23°C | ISO 11359-2 | 2E-05 cm/cm/°C | |
| TD：-40to23°C | ISO 11359-2 | 5.7E-05 cm/cm/°C | |
| MD：-- | ISO 11359-2 | 2E-05 cm/cm/°C | |
| TD：55to160°C | ISO 11359-2 | 1E-04 cm/cm/°C | |
| Heat distortion temperature | 0.45MPa,未退火，HDT | ISO 75-2/B | 300 °C |
| 1.8MPa,未退火，HDT | ISO 75-2/A | 282 °C |