PP 8650 TOTAL USA
168
- Unit Price:US$ 1,536 /MT
- Packaging Specification:25 KG/PKG
- Packaging Material:Paper bag
- Supply Quantity:10MT
- Delivery Terms:FOB
- Port of Loading :China Main Port
- Accepted Payment Methods:T/T
- Shipping:Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 ********View
serv********View
For more details, please contact the supplier!
Material Description
- Material Properties:--
- Application Areas:--
- Color:--
- Grade:Withdrawal level
Technical Data Sheet
Compare
| physical property | Test Condition | Test Method | Test Result |
|---|---|---|---|
| 230°C/2.16kg | g/10min | 0.20to28 | |
| Melt volume flow rate | ISO 527-2/5 | 0.01to0.25 | |
| 230°C/2.16kg | g/10min | 0.25to38 | |
| spiral flow length | mm | 500.38to800.10 | |
| Flow: 23 ℃ | mm/mm | 0.330to0.457 | |
| Apparent density | g/cm³ | 0.52to0.53 |
| hardness | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Shore hardness | 75to98 | ||
| Rockwell hardness | 58to68 | ||
| ball-indentation hardness | 44.83to60.0 MPa |
| optical performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| gloss | 79to132 | ||
| Haze ratio | % | 0.40to17 |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Impact strength of simply supported beam without notch | kJ/m² | 1.114to45.037 | |
| Suspended wall beam without notch impact strength | J/m | 0.013to0.024 | |
| Dart impact | N.m | 1831.86to2831.86 |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Yield, 23 ℃ | % | 6.0to28 | |
| 19.59to31.38 MPa | |||
| Tensile modulus | 0.15to1.0 | ||
| Yield, 23 ℃ | 24.41to30.48 MPa | ||
| Fracture, 23 ℃ | % | 78to510 | |
| 19.31to44.34 MPa | |||
| % | 46to510 | ||
| bending strength | 6.5to25.03 MPa | ||
| Fracture, 23 ℃ | 14.48to40.0 MPa | ||
| Yield, 23 ℃ | % | 10to16 | |
| Flexural modulus | 737.93to827.59 MPa |
| film | Test Condition | Test Method | Test Result |
|---|---|---|---|
| MD: Surrender | 18.0to22.62 MPa | ||
| MD | 344.83to793.1 MPa | ||
| film thickness | 2.0to3.1 | ||
| Fracture, 23 ℃ | % | 500to760 | |
| 29.03to39.59 MPa | |||
| MD: Fracture | 20.34to40.55 MPa | ||
| % | 490to760 | ||
| Dart impact | J | 0.54to16.45 | |
| Initial sealing temperature | °C | 105to115 |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| 0.45MPa, Not annealed | °C | 54to85 | |
| 1.8MPa, Not annealed | °C | 48to55 | |
| 0.45MPa, Not annealed | °C | 72to100 | |
| 1.8MPa, Not annealed | °C | 45to96 |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.