Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PP 8650 TOTAL USA
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | TOTAL USA/8650 |
|---|---|---|---|
| Impact strength of simply supported beam without notch | 23℃ | kJ/m² | 1.114to45.037 |
| Dart impact | 23℃ | N.m | 1831.86to2831.86 |
| Suspended wall beam without notch impact strength | 23℃ | J/m | 0.013to0.024 |
| hardness | Test Condition | Test Method | TOTAL USA/8650 |
|---|---|---|---|
| Shore hardness | 23℃ | 75to98 | |
| ball-indentation hardness | 44.83to60.0 MPa | ||
| Rockwell hardness | 23℃ | 58to68 |
| film | Test Condition | Test Method | TOTAL USA/8650 |
|---|---|---|---|
| Fracture, 23 ℃ | % | 500to760 | |
| film thickness | 2.0to3.1 | ||
| Fracture, 23 ℃ | 29.03to39.59 MPa | ||
| MD: Fracture | % | 490to760 | |
| MD: Surrender | 18.0to22.62 MPa | ||
| Initial sealing temperature | °C | 105to115 | |
| MD: Fracture | 20.34to40.55 MPa | ||
| Dart impact | 23℃ | J | 0.54to16.45 |
| MD | 344.83to793.1 MPa |
| Mechanical properties | Test Condition | Test Method | TOTAL USA/8650 |
|---|---|---|---|
| Yield, 23 ℃ | 24.41to30.48 MPa | ||
| % | 10to16 | ||
| Tensile modulus | 摩擦系数 | 0.15to1.0 | |
| Fracture, 23 ℃ | 14.48to40.0 MPa | ||
| Flexural modulus | 23℃ | 737.93to827.59 MPa | |
| Fracture, 23 ℃ | % | 46to510 | |
| bending strength | 23℃ | 6.5to25.03 MPa |
| optical performance | Test Condition | Test Method | TOTAL USA/8650 |
|---|---|---|---|
| gloss | 79to132 | ||
| Haze ratio | % | 0.40to17 |
| physical property | Test Condition | Test Method | TOTAL USA/8650 |
|---|---|---|---|
| 230°C/2.16kg | g/10min | 0.25to38 | |
| Flow: 23 ℃ | 流动,23℃ | mm/mm | 0.330to0.457 |
| Melt volume flow rate | 230°C/2.16kg | ISO 527-2/5 | 0.01to0.25 |
| spiral flow length | mm | 500.38to800.10 | |
| Apparent density | g/cm³ | 0.52to0.53 |
| Thermal performance | Test Condition | Test Method | TOTAL USA/8650 |
|---|---|---|---|
| 0.45MPa, Not annealed | °C | 72to100 | |
| 1.8MPa, Not annealed | °C | 45to96 |