PA6

PA6 Ultramid® B3WG3 BASF GERMANY

226

Unit Price:US$ 1,731 /MT
Packaging Specification:
25 KG/PKG
Packaging Material:
Paper bag
Supply Quantity:
20MT
Delivery Terms:
FOB
Port of Loading :
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View

serv********View

+86 ********View

For more details, please contact the supplier!

Material Description

Material Properties:Thermal stability｜Oil resistant
Application Areas:Shell｜Gears
Color:--
Grade:Injection grade

Material Certification

Technical Data Sheet

other	Test Condition	Test Method	Test Result
remarks			缩模率:0.45
characteristic			15%玻璃纤维增强注塑级.用于热老化部件.

impact performance	Test Condition	Test Method	Test Result
Impact strength of simply supported beam without notch	23°C	ISO 179	40 kJ/m²

flammability	Test Condition	Test Method	Test Result
UL flame retardant rating	3.0mm	UL 94	HB
	UL flame retardant rating	0.8mm	UL 94	HB
	UL flame retardant rating	UL flame retardant rating	1.5mm	UL 94	HB

mechanical properties	Test Condition	Test Method	Test Result
Tensile modulus	23°C	ISO 527-2	5800 Mpa
tensile strength	Break,23°C	ISO 527-2	130 Mpa
Tensile strain	Break,23°C	ISO 527-2	3.5 %
Bending modulus	23°C	ISO 178	5400 Mpa
Tensile stress	干燥	ISO 527-2	130 MPa
bending strength	干燥	MPa	IS 178 180
Charpy Notched Impact Strength		ASTM D256/ISO 179	6 kg·cm/cm(J/M)ft·lb/in
	Charpy Notched Impact Strength		ASTM D256/ISO 179	45 kg·cm/cm(J/M)ft·lb/in
		Charpy Notched Impact Strength		ASTM D256/ISO 179	50 kg·cm/cm(J/M)ft·lb/in
		Charpy Notched Impact Strength	Charpy Notched Impact Strength		ASTM D256/ISO 179	5 kg·cm/cm(J/M)ft·lb/in
Elongation at Break		ASTM D638/ISO 527	3.5 %
Tensile modulus		ASTM D638/ISO 527	5800 kg/cm²(MPa)[Lb/in²]
tensile strength		ASTM D638/ISO 527	130(断裂) kg/cm²(MPa)[Lb/in²]
Bending modulus		ASTM D790/ISO 178	5300 kg/cm²(MPa)[Lb/in²]
bending strength		ASTM D790/ISO 178	200 kg/cm²(MPa)[Lb/in²]

thermal performance	Test Condition	Test Method	Test Result
Hot deformation temperature	1.8MPa,Unannealed	ISO 75-2/A	190 °C
Melting temperature		ISO 3146	220 °C
RTI Elec	0.8mm	UL 746	130 °C
	RTI Elec	1.5mm	UL 746	130 °C
	RTI Elec	RTI Elec	3.0mm	UL 746	130 °C
RTI Imp	1.5mm	UL 746	85.0 °C
RTI Imp	RTI Imp	3.0mm	UL 746	85.0 °C
RTI Str	1.5mm	UL 746	130 °C
RTI Str	RTI Str	3.0mm	UL 746	130 °C
UL flame retardant rating		UL94	HB
Hot deformation temperature	1.8Mpa	ISO 75-2	190 ℃
Hot deformation temperature	Hot deformation temperature	0.45Mpa	ISO 75-2	215 ℃
Combustibility (rate)		UL 94	HB
Hot deformation temperature	HDT	ASTM D648/ISO 75	198 ℃（℉）
Hot deformation temperature	Hot deformation temperature	HDT	ASTM D648/ISO 75	218 ℃（℉）

Physical properties	Test Method	Test Result
density	ASTM D792/ISO 1183	1230
Shrinkage rate	ASTM D955	0.45 %
Water absorption rate	ASTM D570/ISO 62	8 %

Electrical performance	Test Condition	Test Method	Test Result
Dielectric constant		IEC 250	3.8
Dielectric loss		IEC 250	250 10
Volume resistivity		IEC 93	Ω.cm
Volume resistivity	Volume resistivity		ASTM D257/IEC 60093	>1E 13 Ω.cm

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.

Get App

Top

PA6 Ultramid® B3WG3 BASF GERMANY

Material Description

Material Certification

Technical Data Sheet Compare

Technical Data Sheet