PA6 B3WG3 BASF GERMANY
Ultramid®
Shell、Gears
Thermal stability、Oil resistant
UL
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | BASF GERMANY/B3WG3 |
|---|---|---|---|
| Impact strength of simply supported beam without notch | 23°C | ISO 179 | 40 kJ/m² |
| Mechanical properties | Test Condition | Test Method | BASF GERMANY/B3WG3 |
|---|---|---|---|
| bending strength | ASTM D790/ISO 178 | 200 kg/cm²(MPa)[Lb/in²] | |
| 干燥 | MPa | IS 178 180 | |
| Tensile strain | 断裂,23°C | ISO 527-2 | 3.5 % |
| Flexural modulus | ASTM D790/ISO 178 | 5300 kg/cm²(MPa)[Lb/in²] | |
| 23°C | ISO 178 | 5400 Mpa | |
| Tensile modulus | 23°C | ISO 527-2 | 5800 Mpa |
| Tensile stress | 干燥 | ISO 527-2 | 130 MPa |
| Tensile modulus | ASTM D638/ISO 527 | 5800 kg/cm²(MPa)[Lb/in²] | |
| tensile strength | 断裂,23°C | ISO 527-2 | 130 Mpa |
| Charpy Notched Impact Strength | ASTM D256/ISO 179 | 5 kg·cm/cm(J/M)ft·lb/in | |
| elongation at break | ASTM D638/ISO 527 | 3.5 % | |
| tensile strength | ASTM D638/ISO 527 | 130(断裂) kg/cm²(MPa)[Lb/in²] |
| Electrical performance | Test Condition | Test Method | BASF GERMANY/B3WG3 |
|---|---|---|---|
| Dielectric loss | IEC 250 | 250 10 | |
| Volume resistivity | IEC 93 | Ω.cm | |
| ASTM D257/IEC 60093 | >1E 13 Ω.cm | ||
| dielectric constant | IEC 250 | 3.8 |
| other | Test Condition | Test Method | BASF GERMANY/B3WG3 |
|---|---|---|---|
| characteristic | 15%玻璃纤维增强注塑级.用于热老化部件. | ||
| notes | 缩模率:0.45 |
| Physical properties | Test Condition | Test Method | BASF GERMANY/B3WG3 |
|---|---|---|---|
| Shrinkage rate | ASTM D955 | 0.45 % | |
| density | ASTM D792/ISO 1183 | 1230 | |
| Water absorption rate | ASTM D570/ISO 62 | 8 % |
| flammability | Test Condition | Test Method | BASF GERMANY/B3WG3 |
|---|---|---|---|
| UL flame retardant rating | 3.0mm | UL 94 | HB |
| 0.8mm | UL 94 | HB | |
| 1.5mm | UL 94 | HB |
| Thermal performance | Test Condition | Test Method | BASF GERMANY/B3WG3 |
|---|---|---|---|
| Combustibility (rate) | UL 94 | HB | |
| Heat distortion temperature | 0.45Mpa，HDT | ISO 75-2 | 215 ℃ |
| RTI Imp | 1.5mm | UL 746 | 85.0 °C |
| RTI Elec | 3.0mm | UL 746 | 130 °C |
| RTI Imp | 3.0mm | UL 746 | 85.0 °C |
| UL flame retardant rating | UL94 | HB | |
| melting temperature | ISO 3146 | 220 °C | |
| RTI Elec | 0.8mm | UL 746 | 130 °C |
| Heat distortion temperature | 1.8Mpa，HDT | ISO 75-2 | 190 ℃ |
| HDT | ASTM D648/ISO 75 | 218 ℃（℉） | |
| 1.8MPa,未退火，HDT | ISO 75-2/A | 190 °C | |
| RTI Str | 1.5mm | UL 746 | 130 °C |
| 3.0mm | UL 746 | 130 °C | |
| RTI Elec | 1.5mm | UL 746 | 130 °C |