PA6

PA6 Ultramid® B3WG7 BASF GERMANY

236

Unit Price:US$ 1,445 /MT
Packaging Specification:
25 KG/PKG
Packaging Material:
Paper bag
Supply Quantity:
20MT
Delivery Terms:
FOB
Port of Loading :
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View

serv********View

+86 ********View

For more details, please contact the supplier!

Material Description

Material Properties:Glass fiber reinforced｜Aging resistance｜heat-resisting
Application Areas:Automotive sector
Color:--
Grade:Enhanced level

Material Certification

Technical Data Sheet

other	Test Condition	Test Method	Test Result
characteristic			良好的耐热老化性能耐油性能
purpose			汽车领域应用

impact performance	Test Condition	Test Method	Test Result
Impact strength of simply supported beam without notch	23°C	ISO 179	100 kJ/m²
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch	-30°C	ISO 179	90 kJ/m²

flammability	Test Condition	Test Method	Test Result
UL flame retardant rating	3.0mm	UL 94	HB
UL flame retardant rating	UL flame retardant rating	1.5mm	UL 94	HB

mechanical properties	Test Condition	Test Method	Test Result
Bending modulus	23°C	ISO 178	10000 Mpa
Tensile strain	Break,-40°C	ISO 527-2	3.8 %
tensile strength	Break,23°C	ISO 527-2	195 Mpa
Tensile modulus	23°C	ISO 527-2	11000 Mpa
Tensile strain	Break,23°C	ISO 527-2	3.5 %

thermal performance	Test Condition	Test Method	Test Result
RTI Str	1.5mm	UL 746	130 °C
RTI Str	RTI Str	3.0mm	UL 746	130 °C
RTI Imp	3.0mm	UL 746	100 °C
RTI Imp	RTI Imp	1.5mm	UL 746	90.0 °C
RTI Elec	3.0mm	UL 746	130 °C
	RTI Elec	1.5mm	UL 746	130 °C
	RTI Elec	RTI Elec	0.75mm	UL 746	130 °C
Linear coefficient of thermal expansion	TD		6.5E-05 cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	MD		1.8E-05 cm/cm/°C
Melting temperature		ISO 3146	220 °C
Hot deformation temperature	1.8MPa,Unannealed	ISO 75-2/A	215 °C
Hot deformation temperature	Hot deformation temperature	0.45MPa,Unannealed	ISO 75-2/B	220 °C

Physical properties	Test Condition	Test Method	Test Result
Water absorption rate	Equilibrium,23°C,50%RH	ISO 62	2.0 %
Water absorption rate	Water absorption rate	Saturation,23°C	ISO 62	6.2 %
Melt Volume Flow Rate (MVR)	275°C/5.0kg	ISO 1133	45.0 cm3/10min
Shrinkage rate		ASTM D955	0.35 %

Electrical performance	Test Condition	Test Method	Test Result
Compared to the anti leakage trace index		IEC 60112	PLC 1
Dissipation factor	1MHz	IEC 60250	0.021
Surface resistivity		IEC 60093	1E+13 ohms
Dielectric constant	1MHz	IEC 60250	3.90
Dissipation factor	100Hz	IEC 60250	0.021

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.

Get App

Top

PA6 Ultramid® B3WG7 BASF GERMANY

Material Description

Material Certification

Technical Data Sheet Compare

Technical Data Sheet