Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PA6 B3WG7 BASF GERMANY
Ultramid®
Automotive sector
Glass fiber reinforced、Aging resistance、heat-resisting
UL
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | BASF GERMANY/B3WG7 |
|---|---|---|---|
| Impact strength of simply supported beam without notch | -30°C | ISO 179 | 90 kJ/m² |
| 23°C | ISO 179 | 100 kJ/m² |
| Mechanical properties | Test Condition | Test Method | BASF GERMANY/B3WG7 |
|---|---|---|---|
| Tensile strain | 断裂,23°C | ISO 527-2 | 3.5 % |
| Flexural modulus | 23°C | ISO 178 | 10000 Mpa |
| Tensile modulus | 23°C | ISO 527-2 | 11000 Mpa |
| tensile strength | 断裂,23°C | ISO 527-2 | 195 Mpa |
| Tensile strain | 断裂,-40°C | ISO 527-2 | 3.8 % |
| Electrical performance | Test Condition | Test Method | BASF GERMANY/B3WG7 |
|---|---|---|---|
| Compared to the Leakage Tracking Index (CTI) | IEC 60112 | PLC 1 | |
| Dissipation Factor | 100Hz | IEC 60250 | 0.021 |
| dielectric constant | 1MHz | IEC 60250 | 3.90 |
| Surface Resistivity | IEC 60093 | 1E+13 ohms | |
| Dissipation Factor | 1MHz | IEC 60250 | 0.021 |
| other | Test Condition | Test Method | BASF GERMANY/B3WG7 |
|---|---|---|---|
| characteristic | 良好的耐热老化性能 耐油性能 | ||
| purpose | 汽车领域应用 |
| Physical properties | Test Condition | Test Method | BASF GERMANY/B3WG7 |
|---|---|---|---|
| Shrinkage rate | ASTM D955 | 0.35 % |
| flammability | Test Condition | Test Method | BASF GERMANY/B3WG7 |
|---|---|---|---|
| UL flame retardant rating | 3.0mm | UL 94 | HB |
| 1.5mm | UL 94 | HB |
| physical property | Test Condition | Test Method | BASF GERMANY/B3WG7 |
|---|---|---|---|
| Water absorption rate | 平衡,23°C,50%RH | ISO 62 | 2.0 % |
| 饱和,23°C | ISO 62 | 6.2 % | |
| Melt volume flow rate | 275°C/5.0kg | ISO 1133 | 45.0 cm3/10min |
| Thermal performance | Test Condition | Test Method | BASF GERMANY/B3WG7 |
|---|---|---|---|
| RTI Imp | 1.5mm | UL 746 | 90.0 °C |
| Heat distortion temperature | 0.45MPa,未退火，HDT | ISO 75-2/B | 220 °C |
| Linear coefficient of thermal expansion | MD | 1.8E-05 cm/cm/°C | |
| Heat distortion temperature | 1.8MPa,未退火，HDT | ISO 75-2/A | 215 °C |
| RTI Str | 1.5mm | UL 746 | 130 °C |
| 3.0mm | UL 746 | 130 °C | |
| RTI Elec | 1.5mm | UL 746 | 130 °C |
| 3.0mm | UL 746 | 130 °C | |
| RTI Imp | 3.0mm | UL 746 | 100 °C |
| Linear coefficient of thermal expansion | TD | 6.5E-05 cm/cm/°C | |
| melting temperature | ISO 3146 | 220 °C | |
| RTI Elec | 0.75mm | UL 746 | 130 °C |