PA66 Zytel® 80G33HSL-NC010 DUPONT USA
155
- Unit Price:US$ 4,815 /MT
- Packaging Specification:25 KG/PKG
- Packaging Material:Paper bag
- Supply Quantity:65MT
- Delivery Terms:FOB
- Port of Loading :China Main Port
- Accepted Payment Methods:T/T
- Shipping:Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 ********View
serv********View
For more details, please contact the supplier!
Material Description
- Material Properties:Low temperature resistance｜wear resistant
- Application Areas:Automotive components｜Electronic and electrical accessories
- Color:--
- Grade:Injection grade
Technical Data Sheet
Compare
| hardness | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Rockwell hardness | M 计秤 | ISO 2039-2 | 70 |
| R 计秤 | ISO 2039-2 | 110 |
| thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Heat Deflection Temperature | 0.45 MPa, 未退火 | ISO 75-2/B | 261 °C |
| 1.8 MPa, 未退火 | ISO 75-2/A | 246 °C | |
| Glass Transition Temperature | ISO 11357-2 | 75.0 °C | |
| vicat | ISO 306/B50 | 245 °C | |
| melting temperature | ISO 11357-3 | 262 °C | |
| Linear coefficient of thermal expansion | 流动 | ISO 11359-2 | 1.5E-5 cm/cm/°C |
| 横向 | ISO 11359-2 | 1.2E-4 cm/cm/°C | |
| Effective thermal diffusivity coefficient | 9.00E-8 m²/s | ||
| Heat Deflection Temperature | 1.8 MPa, 未退火 | ISO 75-2/A | 245 °C |
| Linear coefficient of thermal expansion | 流动 | ISO 11359-2 | 2.4E-5 cm/cm/°C |
| 流动 : -40 到 23°C | ISO 11359-2 | 2.5E-5 cm/cm/°C | |
| 流动 : 55 到 160°C | ISO 11359-2 | 9.0E-6 cm/cm/°C | |
| 横向 | ISO 11359-2 | 1.0E-4 cm/cm/°C | |
| 横向 : -40 到 23°C | ISO 11359-2 | 9.6E-5 cm/cm/°C | |
| 横向 : 55 到 160°C | ISO 11359-2 | 1.2E-4 cm/cm/°C |
| flammability | Test Condition | Test Method | Test Result |
|---|---|---|---|
| burning rate | 1.00 mm | ISO 3795 | 23 mm/min |
| UL flame retardant rating | UL 94 | HB | |
| UL 94 | HB | ||
| FMVSS combustion rate | FMVSS 302 | SE/B | |
| 雾化 - G-value (condensate) | ISO 6452 | 8.0E-4 g |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Impact strength of simply supported beam without notch | -30°C | ISO 179/1eU | 110 kJ/m² |
| 23°C | ISO 179/1eU | 97 kJ/m² | |
| Suspended wall beam without notch impact strength | -30°C | ISO 180/1U | 80 kJ/m² |
| 23°C | ISO 180/1U | 80 kJ/m² | |
| Impact strength of simply supported beam without notch | -40°C | ISO 179/1eU | 110 kJ/m² |
| Filling analysis | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Melt density | 1.12 g/cm³ | ||
| Ejection Temperature | 210 °C | ||
| Specific Heat Capacity of Melt | 2200 J/kg/°C | ||
| Thermal Conductivity of Melt | 0.22 W/m/K | ||
| Emission of Organic Compounds | VDA 277 | 25.0 µgC/g | |
| Odor | VDA 270 | 3.00 | |
| Emission of Organic Compounds | VDA 277 | 25.3 µgC/g |
| Physical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| shrinkage rate | 横向流量 | ISO 294-4 | 0.70 % |
| 流量 | ISO 294-4 | 0.30 % | |
| Water absorption rate | 24 hr, 23°C | ISO 62 | 0.85 % |
| 饱和, 23°C, 2.00 mm | ISO 62 | 4.5 % | |
| 平衡, 23°C, 2.00 mm, 50% RH | ISO 62 | 1.5 % | |
| viscosity number | 96% H2SO4 | ISO 307 | 144 cm³/g |
| Water absorption rate | 24 hr, 23°C | ISO 62 | 0.91 % |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Surface Resistivity | IEC 62631-3-2 | -- ohms | |
| volume resistivity | IEC 62631-3-1 | > 1.0E+13 ohms·m | |
| Compared to the Leakage Tracking Index (CTI) | IEC 60112 | V |
| injection | Test Condition | Test Method | Test Result |
|---|---|---|---|
| drying temperature | 80 °C | ||
| Drying time - hot air dryer | 2.0 to 4.0 hr | ||
| Suggested maximum moisture content | 0.20 % | ||
| Processing (melt) temperature | 285 to 305 °C | ||
| Melt Temperature, Optimum | 295 °C | ||
| mold temperature | 50 to 100 °C | ||
| Mold Temperature, Optimum | 80 °C | ||
| pressure holding | 50.0 to 100 Mpa | ||
| Drying Recommended | yes | ||
| Hold Pressure Time | 3.00 s/mm | ||
| Maximum Screw Tangential Speed | 12 m/min |
| mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Tensile modulus | ISO 527-2 | 8900 Mpa | |
| tensile strength | 断裂 | ISO 527-2 | 146 Mpa |
| Tensile strain | 断裂 | ISO 527-2 | 3.7 % |
| Tensile creep modulus | 1 hr | ISO 899-1 | -- Mpa |
| 1000 hr | ISO 899-1 | -- Mpa | |
| flexural modulus | ISO 178 | 7500 Mpa | |
| Tensile modulus | ISO 527-2 | 8800 Mpa | |
| tensile strength | 断裂 | ISO 527-2 | 148 Mpa |
| Tensile strain | 断裂 | ISO 527-2 | 3.6 % |
| flexural modulus | ISO 178 | 7600 Mpa | |
| bending strength | ISO 178 | 214 Mpa |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.