PA66 80G33HSL-NC010 DUPONT USA
Zytel® 
Automotive components,Electronic and electrical accessories
Low temperature resistanc,wear resistant
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--

Plastic Datasheets

Impact resistanceTest ConditionTest MethodDUPONT USA/80G33HSL-NC010
Suspended wall beam without notch impact strength-30°CISO 180/1U80 kJ/m²
23°CISO 180/1U80 kJ/m²
Impact strength of simply supported beam without notch-40°CISO 179/1eU110 kJ/m²
23°CISO 179/1eU97 kJ/m²
-30°CISO 179/1eU110 kJ/m²
hardnessTest ConditionTest MethodDUPONT USA/80G33HSL-NC010
Rockwell hardnessM 计秤ISO 2039-270
R 计秤ISO 2039-2110
thermal performanceTest ConditionTest MethodDUPONT USA/80G33HSL-NC010
Linear coefficient of thermal expansion流动 : 55 到 160°CISO 11359-29.0E-6 cm/cm/°C
Heat Deflection Temperature1.8 MPa, 未退火，HDTISO 75-2/A245 °C
Linear coefficient of thermal expansion流动ISO 11359-22.4E-5 cm/cm/°C
横向ISO 11359-21.0E-4 cm/cm/°C
Heat Deflection Temperature0.45 MPa, 未退火，HDTISO 75-2/B261 °C
Linear coefficient of thermal expansion横向 : 55 到 160°CISO 11359-21.2E-4 cm/cm/°C
横向 : -40 到 23°CISO 11359-29.6E-5 cm/cm/°C
vicatISO 306/B50245 °C
Linear coefficient of thermal expansion流动 : -40 到 23°CISO 11359-22.5E-5 cm/cm/°C
Effective thermal diffusivity coefficient9.00E-8 m²/s
Glass Transition TemperatureISO 11357-275.0 °C
melting temperatureISO 11357-3262 °C
mechanical propertiesTest ConditionTest MethodDUPONT USA/80G33HSL-NC010
Tensile modulusISO 527-28800 Mpa
tensile strength断裂ISO 527-2148 Mpa
Tensile strain断裂ISO 527-23.6 %
bending strengthISO 178214 Mpa
Tensile creep modulus1 hrISO 899-1-- Mpa
1000 hrISO 899-1-- Mpa
flexural modulusISO 1787600 Mpa
Electrical performanceTest ConditionTest MethodDUPONT USA/80G33HSL-NC010
volume resistivityIEC 62631-3-1> 1.0E+13 ohms·m
Surface ResistivityIEC 62631-3-2-- ohms
Compared to the Leakage Tracking Index (CTI)IEC 60112 V
Physical propertiesTest ConditionTest MethodDUPONT USA/80G33HSL-NC010
shrinkage rate流量ISO 294-40.30 %
Water absorption rate饱和, 23°C, 2.00 mmISO 624.5 %
shrinkage rate横向流量ISO 294-40.70 %
Water absorption rate平衡, 23°C, 2.00 mm, 50% RHISO 621.5 %
24 hr, 23°CISO 620.91 %
viscosity number96% H2SO4ISO 307144 cm³/g
flammabilityTest ConditionTest MethodDUPONT USA/80G33HSL-NC010
雾化 - G-value (condensate)ISO 64528.0E-4 g
UL flame retardant ratingUL 94HB
FMVSS combustion rateFMVSS 302SE/B
burning rate1.00 mmISO 379523 mm/min
Filling analysisTest ConditionTest MethodDUPONT USA/80G33HSL-NC010
Ejection Temperature210 °C
OdorVDA 2703.00
Thermal Conductivity of Melt0.22 W/m/K
Melt density1.12 g/cm³
Emission of Organic CompoundsVDA 27725.3 µgC/g
Specific Heat Capacity of Melt2200 J/kg/°C
injectionTest ConditionTest MethodDUPONT USA/80G33HSL-NC010
pressure holding50.0 to 100 Mpa
Maximum Screw Tangential Speed12 m/min
pressure holdingDrying Recommendedyes
Suggested maximum moisture content0.20 %
Drying time - hot air dryer2.0 to 4.0 hr
Processing (melt) temperature285 to 305 °C
mold temperature50 to 100 °C
drying temperature80 °C
Melt Temperature, Optimum295 °C
Hold Pressure Time3.00 s/mm
Mold Temperature, Optimum80 °C