Material Properties:enhance｜Glass fiber reinforced
Application Areas:Electronic communication accessories｜Electronic communication accessories
Color:--
Grade:Injection grade

Technical Data Sheet Compare

other	Test Condition	Test Method	Test Result
characteristic			玻纤增强
Color			本白色
purpose			车辆配件

thermal performance	Test Condition	Test Method	Test Result
Heat Deflection Temperature	0.45 MPa, 未退火, 3.20 mm	ASTM D648	142 °C
	Heat Deflection Temperature	1.8 MPa, 未退火, 3.20 mm	ASTM D648	134 °C
	Heat Deflection Temperature	Heat Deflection Temperature	1.8 MPa, 未退火, 4.00 mm, 64.0 mm 跨距8	ISO 75-2/Af	133 °C
vicat	--	ASTM D15259	142 °C
vicat	vicat	--	ISO 306/B120	144 °C
Linear coefficient of thermal expansion	流动 : -40 到 40°C	ASTM E831	2.5E-5 cm/cm/°C
	Linear coefficient of thermal expansion	流动 : -40 到 40°C	ISO 11359-2	3.0E-5 cm/cm/°C
		Linear coefficient of thermal expansion	横向 : -40 到 40°C	ASTM E831	7.5E-5 cm/cm/°C
		Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	横向 : -40°C	ISO 11359-2	7.5E-5 cm/cm/°C

flammability	Test Condition	Test Method	Test Result
UL flame retardant rating	1.5 mm	UL 94	V-1

Physical properties	Test Condition	Test Method	Test Result
melt mass-flow rate	280°C/5.0 kg	ASTM D1238	3.5 g/10 min
Melt volume flow rate	280°C/5.0 kg	ISO 1133	3.00 cm3/10min
shrinkage rate	3.20 mm，Flow	内部方法	0.20 - 0.50 %
water absorption rate	24 hr, 23°C	ISO 62	0.11 %
water absorption rate	water absorption rate	24 hr, 23°C2	ISO 62	0.040 %

Electrical performance	Test Condition	Test Method	Test Result
surface resistivity		ASTM D257	1.3E+17 ohms
volume resistivity		ASTM D257	2.0E+16 ohms·cm
dielectric strength	1.60 mm, in Oil	ASTM D149	26 KV/mm
dielectric strength	dielectric strength	1.50 mm, 在油中	IEC 60243-1	26 KV/mm
dielectric constant	1 MHz	ASTM D150	2.93
dielectric constant	dielectric constant	1 MHz	IEC 60250	2.90
Dissipation Factor	1 MHz	ASTM D150	3.4E-3

injection	Test Condition	Test Method	Test Result
drying temperature			110 to 120 °C
drying time			3.0 to 4.0 hr
Suggested maximum moisture content			0.020 %
Suggested injection volume			30 to 70 %
Temperature at the rear of the barrel			265 to 315 °C
Temperature in the middle of the barrel			275 to 320 °C
Temperature at the front of the material cylinder			290 to 325 °C
Spray nozzle temperature			300 to 325 °C
Processing (melt) temperature			300 to 325 °C
mold temperature			80 to 110 °C
Back pressure			0.300 to 0.700 Mpa
screw speed			20 to 100 rpm

mechanical properties	Test Condition	Test Method	Test Result
tensile modulus	--3	ASTM D638	7100 Mpa
tensile modulus	tensile modulus	--	ISO 527-2/1	6400 Mpa
tensile strength	断裂4	ASTM D638	120 Mpa
tensile strength	tensile strength	断裂	ISO 527-2/50	100 Mpa
elongation	断裂4	ASTM D638	3.0 %
elongation	elongation	断裂	ISO 527-2/50	2.5 %
flexural modulus	50.0 mm 跨距5	ASTM D790	5500 Mpa
flexural modulus	flexural modulus	--6	ISO 178	5600 Mpa
bending strength	--6,7	ISO 178	150 Mpa
bending strength	bending strength	屈服, 50.0 mm 跨距5	ASTM D790	140 Mpa

impact performance	Test Condition	Test Method	Test Result
Suspended wall beam without notch impact strength	23°C	ASTM D4812	520 J/m
	Suspended wall beam without notch impact strength	-30°C8	ISO 180/1U	27 kJ/m²
	Suspended wall beam without notch impact strength	Suspended wall beam without notch impact strength	23°C8	ISO 180/1U	28 kJ/m²
Dart impact	23°C, Total Energy	ASTM D3763	18.0 J

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.