Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PPO SE1GFN2 WH50030 SABIC INNOVATIVE US
NORYL™
Electronic communication 、Electronic communication
enhance、Glass fiber reinforced
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | SABIC INNOVATIVE US/SE1GFN2 WH50030 |
|---|---|---|---|
| Suspended wall beam without notch impact strength | -30°C8 | ISO 180/1U | 27 kJ/m² |
| 23°C8 | ISO 180/1U | 28 kJ/m² | |
| 23°C | ASTM D4812 | 520 J/m | |
| Dart impact | 23°C, Total Energy | ASTM D3763 | 18.0 J |
| Mechanical properties | Test Condition | Test Method | SABIC INNOVATIVE US/SE1GFN2 WH50030 |
|---|---|---|---|
| elongation | 断裂4 | ASTM D638 | 3.0 % |
| Tensile modulus | --3 | ASTM D638 | 7100 Mpa |
| Flexural modulus | 50.0 mm 跨距5 | ASTM D790 | 5500 Mpa |
| elongation | 断裂 | ISO 527-2/50 | 2.5 % |
| tensile strength | 断裂4 | ASTM D638 | 120 Mpa |
| bending strength | --6,7 | ISO 178 | 150 Mpa |
| Flexural modulus | --6 | ISO 178 | 5600 Mpa |
| bending strength | 屈服, 50.0 mm 跨距5 | ASTM D790 | 140 Mpa |
| Tensile modulus | -- | ISO 527-2/1 | 6400 Mpa |
| tensile strength | 断裂 | ISO 527-2/50 | 100 Mpa |
| Electrical performance | Test Condition | Test Method | SABIC INNOVATIVE US/SE1GFN2 WH50030 |
|---|---|---|---|
| dielectric strength | 1.60 mm, in Oil | ASTM D149 | 26 KV/mm |
| Volume resistivity | ASTM D257 | 2.0E+16 ohms·cm | |
| Surface Resistivity | ASTM D257 | 1.3E+17 ohms | |
| dielectric constant | 1 MHz | ASTM D150 | 2.93 |
| dielectric strength | 1.50 mm, 在油中 | IEC 60243-1 | 26 KV/mm |
| Dissipation Factor | 1 MHz | ASTM D150 | 3.4E-3 |
| dielectric constant | 1 MHz | IEC 60250 | 2.90 |
| other | Test Condition | Test Method | SABIC INNOVATIVE US/SE1GFN2 WH50030 |
|---|---|---|---|
| characteristic | 玻纤增强 | ||
| Color | 本白色 | ||
| purpose | 车辆配件 |
| flammability | Test Condition | Test Method | SABIC INNOVATIVE US/SE1GFN2 WH50030 |
|---|---|---|---|
| UL flame retardant rating | 1.5 mm | UL 94 | V-1 |
| physical property | Test Condition | Test Method | SABIC INNOVATIVE US/SE1GFN2 WH50030 |
|---|---|---|---|
| melt mass-flow rate | 280°C/5.0 kg | ASTM D1238 | 3.5 g/10 min |
| Water absorption rate | 24 hr, 23°C2 | ISO 62 | 0.040 % |
| 24 hr, 23°C | ISO 62 | 0.11 % | |
| Melt volume flow rate | 280°C/5.0 kg | ISO 1133 | 3.00 cm3/10min |
| Shrinkage rate | 3.20 mm，Flow | 内部方法 | 0.20 - 0.50 % |
| Thermal performance | Test Condition | Test Method | SABIC INNOVATIVE US/SE1GFN2 WH50030 |
|---|---|---|---|
| Linear coefficient of thermal expansion | 流动 : -40 到 40°C | ASTM E831 | 2.5E-5 cm/cm/°C |
| vicat | -- | ISO 306/B120 | 144 °C |
| -- | ASTM D15259 | 142 °C | |
| Linear coefficient of thermal expansion | 横向 : -40°C | ISO 11359-2 | 7.5E-5 cm/cm/°C |
| 流动 : -40 到 40°C | ISO 11359-2 | 3.0E-5 cm/cm/°C | |
| Heat distortion temperature | 0.45 MPa, 未退火, 3.20 mm，HDT | ASTM D648 | 142 °C |
| 1.8 MPa, 未退火, 4.00 mm, 64.0 mm 跨距8，HDT | ISO 75-2/Af | 133 °C | |
| Linear coefficient of thermal expansion | 横向 : -40 到 40°C | ASTM E831 | 7.5E-5 cm/cm/°C |
| Heat distortion temperature | 1.8 MPa, 未退火, 3.20 mm，HDT | ASTM D648 | 134 °C |
| injection | Test Condition | Test Method | SABIC INNOVATIVE US/SE1GFN2 WH50030 |
|---|---|---|---|
| drying time | 3.0 to 4.0 hr | ||
| screw speed | 20 to 100 rpm | ||
| Suggested maximum moisture content | 0.020 % | ||
| Temperature in the middle of the barrel | 275 to 320 °C | ||
| Temperature at the rear of the barrel | 265 to 315 °C | ||
| Processing (melt) temperature | 300 to 325 °C | ||
| drying temperature | 110 to 120 °C | ||
| Suggested injection volume | 30 to 70 % | ||
| Temperature at the front of the material cylinder | 290 to 325 °C | ||
| Back pressure | 0.300 to 0.700 Mpa | ||
| Temperature | 80 to 110 °C | ||
| Spray nozzle temperature | 300 to 325 °C |