PPS

PPS LNP™ LUBRICOMP™ OCF-100-10MG SABIC INNOVATIVE US

245

Unit Price:US$ 4,421 /MT
Packaging Specification:
25 KG/PKG
Packaging Material:
Paper bag
Supply Quantity:
20MT
Delivery Terms:
FOB
Port of Loading :
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View

serv********View

+86 ********View

For more details, please contact the supplier!

Material Description

Material Properties:enhance｜Filler: Glass fiber reinforced material｜30%｜Filler by weight｜Carbon fiber reinforced materials
Application Areas:Electronic and electrical components｜Microswitch
Color:--
Grade:Injection grade

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result
Suspended wall beam without notch impact strength	23°C	ASTM D4812	260 J/m
Suspended wall beam without notch impact strength	Suspended wall beam without notch impact strength	23°C7	ISO 180/1U	14 kJ/m²

mechanical properties	Test Condition	Test Method	Test Result
bending strength	Break,50.0mmSpan4	ASTM D790	206 Mpa
	bending strength	Yield,50.0mmSpan4	ASTM D790	206 Mpa
	bending strength	bending strength	--5,6	ISO 178	46.0 Mpa
Bending modulus	--5	ISO 178	20600 Mpa
Bending modulus	Bending modulus	50.0mmSpan4	ASTM D790	19100 Mpa
elongation	Break	ISO 527-2/5	0.56 %
	elongation	Break3	ASTM D638	0.74 %
		elongation	Yield	ISO 527-2/5	0.56 %
		elongation	elongation	Yield3	ASTM D638	0.74 %
tensile strength	Break	ISO 527-2/5	133 Mpa
	tensile strength	Break3	ASTM D638	157 Mpa
		tensile strength	Yield	ISO 527-2/5	133 Mpa
		tensile strength	tensile strength	Yield3	ASTM D638	157 Mpa
Tensile modulus	--	ISO 527-2/1	28600 Mpa
Tensile modulus	Tensile modulus	--2	ASTM D638	30300 Mpa

thermal performance	Test Condition	Test Method	Test Result
Linear coefficient of thermal expansion	TD:23to60°C	ISO 11359-2	4.6E-06 cm/cm/°C
	Linear coefficient of thermal expansion	TD:-40to40°C	ASTME831	4.6E-06 cm/cm/°C
		Linear coefficient of thermal expansion	MD:23to60°C	ISO 11359-2	1E-06 cm/cm/°C
		Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	MD:-40to40°C	ASTME831	1E-06 cm/cm/°C
Hot deformation temperature	1.8MPa,Unannealed,64.0mmSpan8	ISO 75-2/Af	268 °C
	Hot deformation temperature	1.8MPa,Unannealed,3.20mm	ASTM D648	267 °C
		Hot deformation temperature	0.45MPa,Unannealed,64.0mmSpan8	ISO 75-2/Bf	281 °C
		Hot deformation temperature	Hot deformation temperature	0.45MPa,Unannealed,3.20mm	ASTM D648	280 °C

Physical properties	Test Condition	Test Method	Test Result
Shrinkage rate	TD:24hr	ASTM D955	0.70-1.0 %
Shrinkage rate	Shrinkage rate	MD:24hr	ASTM D955	0.10-0.40 %

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.

Get App

Top

PPS LNP™ LUBRICOMP™ OCF-100-10MG SABIC INNOVATIVE US

Material Description

Technical Data Sheet Compare

Technical Data Sheet