Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PPS OCF-100-10MG SABIC INNOVATIVE US
LNP™ LUBRICOMP™
Electronic and electrical、Microswitch
enhance、Filler: Glass fiber reinf、30%、Filler by weight、Carbon fiber reinforced m
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | SABIC INNOVATIVE US/OCF-100-10MG |
|---|---|---|---|
| Suspended wall beam without notch impact strength | 23°C | ASTM D4812 | 260 J/m |
| 23°C7 | ISO 180/1U | 14 kJ/m² |
| Mechanical properties | Test Condition | Test Method | SABIC INNOVATIVE US/OCF-100-10MG |
|---|---|---|---|
| Tensile modulus | --2 | ASTM D638 | 30300 Mpa |
| bending strength | 屈服,50.0mm跨距4 | ASTM D790 | 206 Mpa |
| tensile strength | 断裂 | ISO 527-2/5 | 133 Mpa |
| 屈服3 | ASTM D638 | 157 Mpa | |
| elongation | 断裂3 | ASTM D638 | 0.74 % |
| Flexural modulus | --5 | ISO 178 | 20600 Mpa |
| 50.0mm跨距4 | ASTM D790 | 19100 Mpa | |
| bending strength | --5,6 | ISO 178 | 46.0 Mpa |
| elongation | 屈服 | ISO 527-2/5 | 0.56 % |
| tensile strength | 屈服 | ISO 527-2/5 | 133 Mpa |
| elongation | 屈服3 | ASTM D638 | 0.74 % |
| tensile strength | 断裂3 | ASTM D638 | 157 Mpa |
| Tensile modulus | -- | ISO 527-2/1 | 28600 Mpa |
| bending strength | 断裂,50.0mm跨距4 | ASTM D790 | 206 Mpa |
| elongation | 断裂 | ISO 527-2/5 | 0.56 % |
| physical property | Test Condition | Test Method | SABIC INNOVATIVE US/OCF-100-10MG |
|---|---|---|---|
| Shrinkage rate | TD:24小时 | ASTM D955 | 0.70-1.0 % |
| MD:24小时 | ASTM D955 | 0.10-0.40 % |
| Thermal performance | Test Condition | Test Method | SABIC INNOVATIVE US/OCF-100-10MG |
|---|---|---|---|
| Linear coefficient of thermal expansion | TD:23到60°C | ISO 11359-2 | 4.6E-06 cm/cm/°C |
| MD:23到60°C | ISO 11359-2 | 1E-06 cm/cm/°C | |
| TD:-40到40°C | ASTME831 | 4.6E-06 cm/cm/°C | |
| Heat distortion temperature | 0.45MPa,未退火,3.20mm，HDT | ASTM D648 | 280 °C |
| 1.8MPa,未退火,64.0mm跨距8，HDT | ISO 75-2/Af | 268 °C | |
| 0.45MPa,未退火,64.0mm跨距8，HDT | ISO 75-2/Bf | 281 °C | |
| 1.8MPa,未退火,3.20mm，HDT | ASTM D648 | 267 °C | |
| Linear coefficient of thermal expansion | MD:-40到40°C | ASTME831 | 1E-06 cm/cm/°C |