PA46 Stanyl® TW271F6 DSM HOLAND
333
- Unit Price:US$ 6,255 /MT
- Packaging Specification:25 KG/PKG
- Packaging Material:Paper bag
- Supply Quantity:23MT
- Delivery Terms:FOB
- Port of Loading :China Main Port
- Accepted Payment Methods:T/T
- Shipping:Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 ********View
serv********View
For more details, please contact the supplier!
Material Description
- Material Properties:Thermal stability｜Lubricity
- Application Areas:Casters｜Automotive Applications
- Color:--
- Grade:Injection grade
Technical Data Sheet
Compare
| thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Heat Deflection Temperature | 0.45 MPa, 未退火 | ISO 75-2/B | 290 °C |
| 1.8 MPa, 未退火 | ISO 75-2/A | 290 °C | |
| melting temperature | ISO 11357-3 | 295 °C | |
| Linear coefficient of thermal expansion | 流动 | ISO 11359-2 | 2.5E-5 cm/cm/°C |
| 横向 | ISO 11359-2 | 6.0E-5 cm/cm/°C | |
| Thermal Index - 5000 hr | IEC 60216 | 177 °C |
| flammability | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Flammability level | UL 94 | HB | |
| UL 94 | HB |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Charpy Notched Impact Strength | -30°C | ISO 179/1eA | 11 kJ/m² |
| 23°C | ISO 179/1eA | 13 kJ/m² | |
| Impact strength of simply supported beam without notch | -30°C | ISO 179/1eU | 65 kJ/m² |
| 23°C | ISO 179/1eU | 85 kJ/m² | |
| Impact strength of cantilever beam gap | -40°C | ISO 180/1A | 11 kJ/m² |
| 23°C | ISO 180/1A | 13 kJ/m² |
| Physical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| density | ISO 1183 | 1.54 g/cm³ | |
| shrinkage rate | 横向流量 | ISO 294-4 | 1.3 % |
| 流量 | ISO 294-4 | 0.50 % | |
| Water absorption rate | 平衡, 23°C, 50% RH | ISO 62 | 2.0 % |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| volume resistivity | IEC 60093 | 1.0E+14 ohms·cm | |
| Compared to the Leakage Tracking Index (CTI) | IEC 60112 | PLC 1 |
| mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Tensile modulus | -- | ISO 527-2 | 10000 Mpa |
| 120°C | ISO 527-2 | 5250 Mpa | |
| 160°C | ISO 527-2 | 4750 Mpa | |
| 180°C | ISO 527-2 | 4500 Mpa | |
| 200°C | ISO 527-2 | 4250 Mpa | |
| tensile strength | 断裂 | ISO 527-2 | 190 Mpa |
| 断裂, 120°C | ISO 527-2 | 100 Mpa | |
| 断裂, 160°C | ISO 527-2 | 85.0 Mpa | |
| 断裂, 180°C | ISO 527-2 | 80.0 Mpa | |
| 断裂, 200°C | ISO 527-2 | 75.0 Mpa | |
| Tensile strain | 断裂 | ISO 527-2 | 3.5 % |
| 断裂, 120°C | ISO 527-2 | 6.5 % | |
| 断裂, 160°C | ISO 527-2 | 6.5 % | |
| 断裂, 180°C | ISO 527-2 | 6.5 % | |
| 断裂, 200°C | ISO 527-2 | 6.5 % | |
| flexural modulus | ISO 178 | 8500 Mpa |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.