Certificates
PA46 TW271F6 DSM HOLAND
Stanyl®
Casters、Automotive Applications
Thermal stability、Lubricity
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | DSM HOLAND/TW271F6 |
|---|---|---|---|
| Charpy Notched Impact Strength | 23°C | ISO 179/1eA | 13 kJ/m² |
| -30°C | ISO 179/1eA | 11 kJ/m² | |
| Impact strength of simply supported beam without notch | 23°C | ISO 179/1eU | 85 kJ/m² |
| Impact strength of cantilever beam gap | 23°C | ISO 180/1A | 13 kJ/m² |
| -40°C | ISO 180/1A | 11 kJ/m² | |
| Impact strength of simply supported beam without notch | -30°C | ISO 179/1eU | 65 kJ/m² |
| Mechanical properties | Test Condition | Test Method | DSM HOLAND/TW271F6 |
|---|---|---|---|
| tensile strength | 断裂, 160°C | ISO 527-2 | 85.0 Mpa |
| Tensile modulus | -- | ISO 527-2 | 10000 Mpa |
| tensile strength | 断裂, 180°C | ISO 527-2 | 80.0 Mpa |
| Tensile strain | 断裂, 120°C | ISO 527-2 | 6.5 % |
| tensile strength | 断裂 | ISO 527-2 | 190 Mpa |
| Tensile modulus | 180°C | ISO 527-2 | 4500 Mpa |
| tensile strength | 断裂, 120°C | ISO 527-2 | 100 Mpa |
| Tensile modulus | 160°C | ISO 527-2 | 4750 Mpa |
| 120°C | ISO 527-2 | 5250 Mpa | |
| Tensile strain | 断裂, 200°C | ISO 527-2 | 6.5 % |
| 断裂, 180°C | ISO 527-2 | 6.5 % | |
| 断裂 | ISO 527-2 | 3.5 % | |
| Flexural modulus | ISO 178 | 8500 Mpa | |
| Tensile strain | 断裂, 160°C | ISO 527-2 | 6.5 % |
| Tensile modulus | 200°C | ISO 527-2 | 4250 Mpa |
| tensile strength | 断裂, 200°C | ISO 527-2 | 75.0 Mpa |
| Electrical performance | Test Condition | Test Method | DSM HOLAND/TW271F6 |
|---|---|---|---|
| Compared to the Leakage Tracking Index (CTI) | IEC 60112 | PLC 1 | |
| Volume resistivity | IEC 60093 | 1.0E+14 ohms·cm |
| flammability | Test Condition | Test Method | DSM HOLAND/TW271F6 |
|---|---|---|---|
| Flammability level | UL 94 | HB |
| physical property | Test Condition | Test Method | DSM HOLAND/TW271F6 |
|---|---|---|---|
| Water absorption rate | 平衡, 23°C, 50% RH | ISO 62 | 2.0 % |
| density | ISO 1183 | 1.54 g/cm³ | |
| Shrinkage rate | 流量 | ISO 294-4 | 0.50 % |
| 横向流量 | ISO 294-4 | 1.3 % |
| Thermal performance | Test Condition | Test Method | DSM HOLAND/TW271F6 |
|---|---|---|---|
| melting temperature | ISO 11357-3 | 295 °C | |
| Heat distortion temperature | 0.45 MPa, 未退火，HDT | ISO 75-2/B | 290 °C |
| 1.8 MPa, 未退火，HDT | ISO 75-2/A | 290 °C | |
| Thermal Index - 5000 hr | IEC 60216 | 177 °C | |
| Linear coefficient of thermal expansion | 流动 | ISO 11359-2 | 2.5E-5 cm/cm/°C |
| 横向 | ISO 11359-2 | 6.0E-5 cm/cm/°C |