PP PRIME POLYPRO J-2000GP PRIME POLYMER JAPAN

475

Unit Price:US$ 1,376 /MT
Packaging Specification:
25 KG/PKG
Packaging Material:
Paper bag
Supply Quantity:
22MT
Delivery Terms:
FOB
Port of Loading :
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View

serv********View

+86 ********View

For more details, please contact the supplier!

Material Description

Material Properties:--
Application Areas:--
Color:--
Grade:Injection grade

Technical Data Sheet

optical performance	Test Condition	Test Method	Test Result
gloss		ASTM D2457	80

impact performance	Test Condition	Test Method	Test Result
Impact strength of simply supported beam without notch	23°C	ISO 179	3.1 kJ/m²

Fracture rate	Test Condition	Test Method	Test Result
optical performance	光滑面	JIS Z8741	80
Thermal Properties	热变形温度，0.45MPa,Unannealed	ISO 75-2/B	93 °C

mechanical properties	Test Condition	Test Method	Test Result
bending strength		ISO 178	42.0 Mpa
Bending modulus		ISO 178	1450 Mpa
Nominal tensile fracture strain		ISO 527-2	50 %
Tensile strain	Break	ISO 527-2	33 %
tensile strength	Yield	ISO 527-2	34.0 Mpa
Tensile modulus		ISO 527-2	1450 Mpa
Bending modulus		ISO 178	1450 Mpa
Tensile strain	Break	ISO 527-2	33 %
Tensile stress	Yield	ISO 527-2	34 Mpa
Tensile modulus		ISO 527-2	1450 Mpa
Elongation at Break	洛氏硬度	ISO 2039-2	99
	Elongation at Break	简支梁Notched冲击强度，23℃	ISO 179	3.1 kJ/m²
	Elongation at Break	Elongation at Break		ISO 527-2	50 %
bending strength		ISO 178	42 Mpa

thermal performance	Test Condition	Test Method	Test Result
Hot deformation temperature	0.45MPa,Unannealed	ISO 75-2/B	93.0 °C

Physical properties	Test Condition	Test Method	Test Result
Shrinkage rate		Internal Method	1.4-1.8 %
melt mass-flow rate	230°C/2.16kg	ISO 1133	21 g/10min
Shrinkage rate		Internal Method	1.4-1.8 %
melt mass-flow rate	230℃,2.16kg	ISO 1133	21 g/10min

hardness	Test Condition	Test Method	Test Result
Rockwell hardness	R-Sale	ISO 2039-2	99

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.

Get App

Top

PP PRIME POLYPRO J-2000GP PRIME POLYMER JAPAN

Material Description

Technical Data Sheet Compare

Technical Data Sheet