Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PP J-2000GP PRIME POLYMER JAPAN
PRIME POLYPRO
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | PRIME POLYMER JAPAN/J-2000GP |
|---|---|---|---|
| Impact strength of simply supported beam without notch | 23°C | ISO 179 | 3.1 kJ/m² |
| hardness | Test Condition | Test Method | PRIME POLYMER JAPAN/J-2000GP |
|---|---|---|---|
| Rockwell hardness | R计秤 | ISO 2039-2 | 99 |
| Fracture rate | Test Condition | Test Method | PRIME POLYMER JAPAN/J-2000GP |
|---|---|---|---|
| optical performance | 光滑面 | JIS Z8741 | 80 |
| Thermal performance | 热变形温度，0.45MPa,未退火 | ISO 75-2/B | 93 °C |
| Mechanical properties | Test Condition | Test Method | PRIME POLYMER JAPAN/J-2000GP |
|---|---|---|---|
| Tensile modulus | ISO 527-2 | 1450 Mpa | |
| Nominal tensile fracture strain | ISO 527-2 | 50 % | |
| bending strength | ISO 178 | 42.0 Mpa | |
| Tensile stress | 屈服 | ISO 527-2 | 34 Mpa |
| Tensile strain | 断裂 | ISO 527-2 | 33 % |
| Flexural modulus | ISO 178 | 1450 Mpa | |
| elongation at break | 洛氏硬度 | ISO 2039-2 | 99 |
| tensile strength | 屈服 | ISO 527-2 | 34.0 Mpa |
| elongation at break | ISO 527-2 | 50 % | |
| 简支梁缺口冲击强度，23℃ | ISO 179 | 3.1 kJ/m² |
| optical performance | Test Condition | Test Method | PRIME POLYMER JAPAN/J-2000GP |
|---|---|---|---|
| gloss | ASTM D2457 | 80 |
| physical property | Test Condition | Test Method | PRIME POLYMER JAPAN/J-2000GP |
|---|---|---|---|
| melt mass-flow rate | 230℃,2.16kg | ISO 1133 | 21 g/10min |
| Shrinkage rate | 内部方法 | 1.4-1.8 % | |
| melt mass-flow rate | 230°C/2.16kg | ISO 1133 | 21 g/10min |
| Thermal performance | Test Condition | Test Method | PRIME POLYMER JAPAN/J-2000GP |
|---|---|---|---|
| Heat distortion temperature | 0.45MPa,未退火，HDT | ISO 75-2/B | 93.0 °C |