ABS

ABS P2H-AT ELIX POLYMERS SPANISH

338

Unit Price:US$ 2,385 /MT
Packaging Specification:
25 KG/PKG
Packaging Material:
Paper bag
Supply Quantity:
40MT
Delivery Terms:
FOB
Port of Loading :
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View

serv********View

+86 ********View

For more details, please contact the supplier!

Material Description

Material Properties:Filler: Glass fiber reinforced material｜16% filler by weight
Application Areas:Application in the automotive field
Color:--
Grade:Anti static level

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result
Impact strength of simply supported beam without notch	-30°C	ISO 179	20 kJ/m²
	Impact strength of simply supported beam without notch	23°C	ISO 179	18 kJ/m²
		Impact strength of simply supported beam without notch	-30°C	ISO 179/1eU	80 kJ/m²
		Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch	23°C	ISO 179/1eU	100 kJ/m²

flammability	Test Condition	Test Method	Test Result
Burning rate	2.00mm	ISO 3795	60 mm/min
UL flame retardant rating	1.6mm	UL 94	HB
Burning wire flammability index	2.0mm	IEC 60695-2-12	700 °C

mechanical properties	Test Condition	Test Method	Test Result
Tensile strain	Break,23°C	ISO 527-2	2.0 %
Bending modulus		ISO 178	5400 Mpa
bending strength		ISO 178	101 Mpa
Tensile modulus		ISO 527-2	5500 Mpa
tensile strength	Yield,23°C	ISO 527-2	74.0 Mpa
tensile strength	tensile strength	Break,23°C	ISO 527-2	74.0 Mpa
Tensile modulus	23°C	ISO 527-2/1	2500 Mpa
tensile strength	Yield,23°C	ISO 527-2/50	44.0 Mpa
Tensile strain	Yield,23°C	ISO 527-2/50	2.1 %
Tensile strain	Tensile strain	Break,23°C	ISO 527-2/50	>15 %
Tensile creep modulus	1hr	ISO 899-1	2200 Mpa
Tensile creep modulus	Tensile creep modulus	1000hr	ISO 899-1	1500 Mpa
Bending modulus	23°C	ISO 178	2400 Mpa
bending strength	23°C	ISO 178	70.0 Mpa

thermal performance	Test Condition	Test Method	Test Result
Hot deformation temperature	0.45MPa,Annealed	ISO 75-2/B	106 °C
Hot deformation temperature	Hot deformation temperature	1.8MPa,Annealed	ISO 75-2/A	102 °C
Vicat softening temperature		ISO 306/B50	105 °C
Linear coefficient of thermal expansion	MD	ISO 11359-1	4E-05 cm/cm/°C
Hot deformation temperature	1.8MPa,Annealed	ISO 75-2/A	93.0 °C
Vicat softening temperature		ISO 306/B50	98.0 °C
Linear coefficient of thermal expansion	MD：23to55°C	ISO 11359-2	9E-05 cm/cm/°C
Hot deformation temperature	0.45MPa,Annealed	ISO 75-2/B	97.0 °C

Physical properties	Test Condition	Test Method	Test Result
Melt Volume Flow Rate (MVR)	220°C/10.0kg	ISO 1133	3.00 cm3/10min
Shrinkage rate		ISO 294-4	0.20-0.40 %
ash content			16 %
Melt Volume Flow Rate (MVR)	220°C/10.0kg	ISO 1133	37.0 cm3/10min
Shrinkage rate	TD	ISO 294-4	0.40-0.60 %
Shrinkage rate	Shrinkage rate	MD	ISO 294-4	0.40-0.60 %

Electrical performance	Test Condition	Test Method	Test Result
Surface resistivity		IEC 60093	1E+14 ohms
Volume resistivity		IEC 60093	>1.0E+15 ohms·cm
Dielectric strength	1.50mm	IEC 60243-1	32 KV/mm
Relative permittivity	100Hz	IEC 60250	2.90
Relative permittivity	Relative permittivity	1MHz	IEC 60250	3.10
Dissipation factor	100Hz	IEC 60250	5E-03
Dissipation factor	Dissipation factor	1MHz	IEC 60250	6E-03
Compared to the anti leakage trace index		IEC 60112	PLC 1
Surface resistivity		IEC 60093	1E+15 ohms
Volume resistivity		IEC 60093	1E+15 ohms·cm
Dielectric strength	23°C,1.00mm	IEC 60243-1	34 KV/mm
Relative permittivity	23°C,100Hz	IEC 60250	3.00
Relative permittivity	Relative permittivity	23°C,1MHz	IEC 60250	2.90
Dissipation factor	23°C,100Hz	IEC 60250	5.5E-03
Dissipation factor	Dissipation factor	23°C,1MHz	IEC 60250	9E-03
Compared to the anti leakage trace index	SolutionA	IEC 60112	PLC 0

hardness	Test Condition	Test Method	Test Result
Ball Pressure Test		ISO 2039-1	135 Mpa
Ball Pressure Test	Ball Pressure Test		ISO 2039-1	110 Mpa

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.

Get App

Top

ABS P2H-AT ELIX POLYMERS SPANISH

Material Description

Technical Data Sheet Compare

Technical Data Sheet