PA66 TECHNYL®  A218V35 SOLVAY FRANCE

313
  • Unit Price:US$ 3,338 /MT
  • Packaging Specification:
    25 KG/PKG
  • Packaging Material:
    Paper bag
  • Supply Quantity:
    78MT
  • Delivery Terms:
    FOB
  • Port of Loading :
    China Main Port
  • Accepted Payment Methods:
    T/T
  • Shipping:
    Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View
serv********View
+86 ********View

For more details, please contact the supplier!

Material Description

  • Material Properties:--
  • Application Areas:--
  • Color:--
  • Grade:Flame retardant grade

Technical Data Sheet

otherTest ConditionTest MethodTest Result
Extreme Oxygen IndexISO 4589-2干燥｜23 %
Normal combustion performance with a thickness of 1.6mm1.60 mm干燥｜HB
UL flame retardant rating1.60 mmUL 94干燥｜HB
mechanical propertiesTest ConditionTest MethodTest Result
tensile strengthBreakISO 527-2/1A干燥｜210 Mpa
Tensile modulusISO 527-2/1A2 ISO 527-22调节后｜8700 Mpa
Tensile modulusISO 527-2/1A2 ISO 527-22干燥｜11400 Mpa
Charpy Notched Impact Strength23℃ISO 179/1eA2干燥｜13.5 kJ/m²
Charpy Notched Impact Strength--ISO 179/1eA调节后｜19 kJ/m²
Tensile strainBreakISO 527-2/1A2调节后｜4.0 %
Tensile strainBreakISO 527-2/1A2干燥｜3.0 %
tensile strengthBreakISO 527-22调节后｜145 Mpa
tensile strengthBreakISO 527-22干燥｜190 Mpa
tensile strengthBreakISO 527-2/1A调节后｜150 Mpa
Impact strength of cantilever beam gapISO 180/1A调节后｜18 kJ/m²
Impact strength of cantilever beam gapISO 180/1A干燥｜13 kJ/m²
Charpy Notched Impact Strength23℃ISO 179/1eU2调节后｜100 kJ/m²
Charpy Notched Impact Strength23℃ISO 179/1eU2干燥｜95.0 kJ/m²
Charpy Notched Impact Strength--ISO 179/1eU调节后｜100 kJ/m²
Charpy Notched Impact Strength--ISO 179/1eU干燥｜95 kJ/m²
Charpy Notched Impact Strength23℃ISO 179/1eA2调节后｜18.5 kJ/m²
Charpy Notched Impact Strength--ISO 179/1eA干燥｜14 kJ/m²
Bending modulusISO 178调节后｜6800 Mpa
Bending modulusISO 178干燥｜9500 Mpa
thermal performanceTest ConditionTest MethodTest Result
Melting temperature-DSC法ISO 3146干燥｜263 °C
Melting temperature--3，DSC法ISO 11357-32干燥｜260 °C
Linear coefficient of thermal expansionFlowISO 11359-22干燥｜0.000022 cm/cm/ ℃
Linear coefficient of thermal expansionAcross Flow: 23 to 85℃ISO 11359-2干燥｜0.000022 cm/cm/ ℃
Physical propertiesTest ConditionTest MethodTest Result
StickinessISO 307干燥｜142 cm³/g
Water absorption rateEquilibriumISO 622干燥｜1.4 %
Water absorption rateSaturationISO 622干燥｜5.5 %
Water absorption rate23 ℃，24hrISO 62干燥｜0.75 %
Electrical performanceTest ConditionTest MethodTest Result
Surface resistivity--IEC 60093干燥｜6.0E+14 Ohm
Surface resistivity--IEC 60093调节后｜1.0E+12 Ohm
Surface resistivity--IEC 600932调节后｜1.0E+12 Ohm
Volume resistivity--IEC 60093干燥｜1.0E+15 ohm.cm
Volume resistivity--IEC 60093调节后｜1.0E+13 ohm.cm
Volume resistivity--IEC 600932干燥｜1.0E+13 ohm.m
Volume resistivity--IEC 600932调节后｜1.0E+11 ohm.m
Relative permittivity--IEC 60250干燥｜3.70
Relative permittivity--IEC 60250调节后｜4.00
Dielectric strengthIEC 60243-1干燥｜34 KV/mm
Dielectric strengthIEC 60243-1调节后｜29 KV/mm
Dissipation factor--IEC 60250调节后｜0.11
Dissipation factor100 HzIEC 60250 2干燥｜0.010
Dissipation factor100 HzIEC 60250 2调节后｜0.15
Dissipation factor1 MHzIEC 60250 2干燥｜0.010
Dissipation factor1 MHzIEC 60250 2调节后｜0.11
Compared to the anti leakage trace indexSolution AIEC 60112 V
Compared to the anti leakage trace indexSolution AIEC 60112 V
Compared to the anti leakage trace index--IEC 601122 V
Relative permittivity100 HzIEC 60250 2干燥｜4.00
Relative permittivity100 HzIEC 60250 2调节后｜9.00
Relative permittivity1 MHzIEC 60250 2干燥｜3.70
Relative permittivity1 MHzIEC 60250 2调节后｜4.00
Dissipation factor--IEC 60250干燥｜0.010
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.