PA66 A218V35 SOLVAY FRANCE
TECHNYL®
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Mechanical properties | Test Condition | Test Method | SOLVAY FRANCE/A218V35 |
|---|---|---|---|
| tensile strength | 断裂 | ISO 527-2/1A | 干燥｜210 Mpa |
| Impact strength of cantilever beam gap | ISO 180/1A | 调节后｜18 kJ/m² | |
| Charpy Notched Impact Strength | -- | ISO 179/1eU | 调节后｜100 kJ/m² |
| 23℃ | ISO 179/1eU2 | 调节后｜100 kJ/m² | |
| Tensile strain | 断裂 | ISO 527-2/1A2 | 调节后｜4.0 % |
| tensile strength | 断裂 | ISO 527-22 | 调节后｜145 Mpa |
| Flexural modulus | ISO 178 | 调节后｜6800 Mpa | |
| Charpy Notched Impact Strength | -- | ISO 179/1eA | 调节后｜19 kJ/m² |
| Tensile modulus | ISO 527-2/1A2 ISO 527-22 | 调节后｜8700 Mpa | |
| Charpy Notched Impact Strength | 23℃ | ISO 179/1eA2 | 干燥｜13.5 kJ/m² |
| Electrical performance | Test Condition | Test Method | SOLVAY FRANCE/A218V35 |
|---|---|---|---|
| relative permittivity | 1 MHz | IEC 60250 2 | 调节后｜4.00 |
| Surface Resistivity | -- | IEC 600932 | 调节后｜1.0E+12 Ohm |
| Dissipation Factor | -- | IEC 60250 | 调节后｜0.11 |
| 100 Hz | IEC 60250 2 | 调节后｜0.15 | |
| relative permittivity | 100 Hz | IEC 60250 2 | 调节后｜9.00 |
| Volume resistivity | -- | IEC 60093 | 调节后｜1.0E+13 ohm.cm |
| Compared to the Leakage Tracking Index (CTI) | 解决方案 A | IEC 60112 | V |
| Surface Resistivity | -- | IEC 60093 | 调节后｜1.0E+12 Ohm |
| dielectric strength | IEC 60243-1 | 调节后｜29 KV/mm | |
| relative permittivity | -- | IEC 60250 | 调节后｜4.00 |
| Volume resistivity | -- | IEC 600932 | 调节后｜1.0E+11 ohm.m |
| Compared to the Leakage Tracking Index (CTI) | -- | IEC 601122 | V |
| Dissipation Factor | 1 MHz | IEC 60250 2 | 调节后｜0.11 |
| other | Test Condition | Test Method | SOLVAY FRANCE/A218V35 |
|---|---|---|---|
| Limiting Oxygen Index | ISO 4589-2 | 干燥｜23 % | |
| UL flame retardant rating | 1.60 mm | UL 94 | 干燥｜HB |
| Normal combustion performance with a thickness of 1.6mm | 1.60 mm | 干燥｜HB |
| physical property | Test Condition | Test Method | SOLVAY FRANCE/A218V35 |
|---|---|---|---|
| Water absorption rate | 饱和 | ISO 622 | 干燥｜5.5 % |
| viscosity number | ISO 307 | 干燥｜142 cm³/g | |
| Water absorption rate | 23 ℃，24hr | ISO 62 | 干燥｜0.75 % |
| 平衡 | ISO 622 | 干燥｜1.4 % |
| Thermal performance | Test Condition | Test Method | SOLVAY FRANCE/A218V35 |
|---|---|---|---|
| Linear coefficient of thermal expansion | 横向: 23 到 85℃ | ISO 11359-2 | 干燥｜0.000022 cm/cm/ ℃ |
| melting temperature | --3，DSC法 | ISO 11357-32 | 干燥｜260 °C |
| -DSC法 | ISO 3146 | 干燥｜263 °C | |
| Linear coefficient of thermal expansion | 流动 | ISO 11359-22 | 干燥｜0.000022 cm/cm/ ℃ |