EAA PRIMACOR™ 1321 STYRON US
359
- Unit Price:US$ 3,506 /MT
- Packaging Specification:25 KG/PKG
- Packaging Material:Paper bag
- Supply Quantity:20MT
- Delivery Terms:FOB
- Port of Loading :China Main Port
- Accepted Payment Methods:T/T
- Shipping:Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 ********View
serv********View
For more details, please contact the supplier!
Material Description
- Material Properties:Heat sealing performance｜Resistance to stress cracking｜high strength｜High toughness
- Application Areas:Food service sector｜Food packaging｜Food containers｜Multi layer composite material food packaging
- Color:--
- Grade:Blow molding grade
Technical Data Sheet
Compare
| physical property | Test Condition | Test Method | Test Result |
|---|---|---|---|
| density | ASTM D-792 | 0.935 g/cm³ | |
| ISO 1183/A | 0.935 g/cm³ | ||
| Content of comonomer | 内部方法 | 6.5 % | |
| melt mass-flow rate | ASTMD1238 | 2.6 g/10min | |
| density | ASTMD792 | 0.935 g/cm³ |
| optical performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| gloss | ASTM D-2457 | 76 | |
| Haze ratio | ASTM D-1003 | 3.7 % | |
| ISO 14782 | 3.7 % | ||
| gloss | ASTM D2457 | 76 | |
| Haze ratio | ISO 14782 | 3.7 % | |
| ASTM D1003 | 3.7 % |
| Basic performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| melt mass-flow rate | ASTM D-1238 | 2.6 g/10min | |
| ISO 1133 | 2.6 g/10min | ||
| Monomer content | Internal Method | 6.5 % |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| tensile strength | ASTM D-638 | 10 MPa | |
| ISO 527-2/508 | 10 MPa | ||
| ASTM D-638 | 20.1 MPa | ||
| ISO 527-3 | 31.8 MPa | ||
| ISO 527-3 | 31.8 MPa | ||
| elongation at break | ASTM D-882 | 510 % | |
| ASTM D-882 | 460 % | ||
| ISO 527-3 | 460 % | ||
| ISO 527-3 | 510 % | ||
| Dart impact | ASTM D-1709B | 410 g | |
| ISO 7765-1/B | 410 g | ||
| Elmendorf tear strength | ASTM D-1922 | 270 g | |
| ASTM D-1922 | 390 g | ||
| tensile strength | ISO 527-2/508 | 20.1 MPa | |
| elongation at break | ASTM D-638 | 640 % | |
| ISO 527-2/508 | 640 % | ||
| tensile strength | ASTM D-882 | 11.3 MPa | |
| ASTM D-882 | 11.1 MPa | ||
| ISO 527-3 | 11.3 MPa | ||
| ISO 527-3 | 11.5 MPa | ||
| ASTM D-882 | 31.8 MPa | ||
| ASTM D-882 | 31.8 MPa | ||
| Elmendorf tear strength | ISO 6383-2 | 1200 N | |
| ISO 6383-2 | 1700 N | ||
| elongation | ISO 527-2/508 | 640 % | |
| ASTM D638 | 640 % | ||
| tensile strength | ISO 527-2/508 | 20.1 Mpa | |
| ASTM D638 | 20.1 Mpa | ||
| ISO 527-2/508 | 10.0 Mpa | ||
| ASTM D638 | 10.0 Mpa |
| film | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Elmendorf tear strength | ASTM D1922 | 390 g | |
| ISO 6383-2 | 1200 N | ||
| ISO 6383-2 | 1700 N | ||
| tensile strength | ASTM D882 | 11.3 Mpa | |
| ASTM D882 | 11.1 Mpa | ||
| ISO 527-3 | 11.3 Mpa | ||
| ISO 527-3 | 11.5 Mpa | ||
| ASTMD882 | 31.8 Mpa | ||
| ASTMD882 | 31.8 Mpa | ||
| elongation | ASTMD882 | 460 % | |
| ASTMD882 | 510 % | ||
| Dart impact | ASTMD1709B | 410 g | |
| Elmendorf tear strength | ASTM D1922 | 270 g |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| vicat | ASTM D-1525 | 88.9 ℃ | |
| ISO 306 | 88.9 ℃ | ||
| melting temperature | 103 ℃ | ||
| vicat | ASTMD1525 | 88.9 °C | |
| melting temperature | 内部方法 | 103 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.