Material Description
- Material Properties:Dimensional stability｜High impact｜High rigidity
- Application Areas:Printer components｜Cold water pipe application｜Water heater
- Color:--
- Grade:Injection grade
Technical Data Sheet
Compare
| physical property | Test Condition | Test Method | Test Result |
|---|---|---|---|
| melt mass-flow rate | ASTM D1238 | 6.0 g/10min | |
| Melt volume flow rate | ISO 1133 | 6.00 cm3/10min | |
| Shrinkage rate | 内部方法 | 0.20-0.25 % | |
| 内部方法 | 0.40-0.60 % |
| flammability | Test Condition | Test Method | Test Result |
|---|---|---|---|
| UL flame retardant rating | UL 94 | HB | |
| Burning wire flammability index | IEC 60695-2-12 | 650 °C |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| tensile strength | ASTM D638 | 101 Mpa | |
| ISO 527-2/5 | 98.0 Mpa | ||
| ASTM D638 | 101 Mpa | ||
| ISO 527-2/5 | 98.0 Mpa | ||
| elongation | ASTM D638 | 2.9 % | |
| Tensile strain | ISO 527-2/5 | 3.2 % | |
| elongation | ASTM D638 | 100 % | |
| Tensile strain | ISO 527-2/5 | 3.2 % | |
| Flexural modulus | ASTM D790 | 6600 Mpa | |
| Tensile modulus | ASTM D638 | 7600 Mpa | |
| ISO 527-2/1 | 7700 Mpa | ||
| Flexural modulus | ISO 178 | 7100 Mpa | |
| bending strength | ISO 178 | 141 Mpa | |
| ASTM D790 | 144 Mpa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Impact strength of simply supported beam without notch | ISO 179/1eU | 36 kJ/m² | |
| ISO 179/1eU | 39 kJ/m² | ||
| Impact strength of cantilever beam gap | ISO 180/1A | 10 kJ/m² | |
| Suspended wall beam without notch impact strength | ISO 180/1U | 42 kJ/m² | |
| ISO 180/1U | 42 kJ/m² | ||
| Dart impact | ASTM D3763 | 10.0 J | |
| ASTM D3763 | 15.0 J |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Linear coefficient of thermal expansion | ISO 11359-2 | 1.2E-04 cm/cm/°C | |
| Heat distortion temperature | ASTM D648 | 166 °C | |
| ISO 75-2/Bf | 168 °C | ||
| ASTM D648 | 156 °C | ||
| ISO 75-2/Af | 153 °C | ||
| vicat | ISO 306/B120 | 150 °C | |
| ball-indentation hardness | IEC 60695-10-2 | Pass | |
| Linear coefficient of thermal expansion | ASTME831 | 2.5E-05 cm/cm/°C | |
| ISO 11359-2 | 2.5E-05 cm/cm/°C | ||
| ASTME831 | 1.3E-04 cm/cm/°C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.