Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PPO PPX830 SABIC INNOVATIVE SHANGHAI
NORYL GTX™
Printer components、Cold water pipe applicati、Water heater
Dimensional stability、High impact、High rigidity
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | SABIC INNOVATIVE SHANGHAI/PPX830 |
|---|---|---|---|
| Suspended wall beam without notch impact strength | -30°C | ISO 180/1U | 42 kJ/m² |
| 23°C | ISO 180/1U | 42 kJ/m² | |
| Dart impact | 23°C,TotalEnergy | ASTM D3763 | 15.0 J |
| -30°C,TotalEnergy | ASTM D3763 | 10.0 J | |
| Impact strength of simply supported beam without notch | 23°C | ISO 179/1eU | 39 kJ/m² |
| Impact strength of cantilever beam gap | 23°C | ISO 180/1A | 10 kJ/m² |
| Impact strength of simply supported beam without notch | -30°C | ISO 179/1eU | 36 kJ/m² |
| Mechanical properties | Test Condition | Test Method | SABIC INNOVATIVE SHANGHAI/PPX830 |
|---|---|---|---|
| Tensile modulus | ISO 527-2/1 | 7700 Mpa | |
| tensile strength | 断裂 | ISO 527-2/5 | 98.0 Mpa |
| elongation | 屈服 | ASTM D638 | 2.9 % |
| Tensile strain | 屈服 | ISO 527-2/5 | 3.2 % |
| tensile strength | 断裂 | ASTM D638 | 101 Mpa |
| Flexural modulus | 50.0mm跨距 | ASTM D790 | 6600 Mpa |
| tensile strength | 屈服 | ISO 527-2/5 | 98.0 Mpa |
| Tensile modulus | ASTM D638 | 7600 Mpa | |
| elongation | 断裂 | ASTM D638 | 100 % |
| bending strength | 屈服,50.0mm跨距 | ASTM D790 | 144 Mpa |
| ISO 178 | 141 Mpa | ||
| Flexural modulus | ISO 178 | 7100 Mpa | |
| Tensile strain | 断裂 | ISO 527-2/5 | 3.2 % |
| tensile strength | 屈服 | ASTM D638 | 101 Mpa |
| flammability | Test Condition | Test Method | SABIC INNOVATIVE SHANGHAI/PPX830 |
|---|---|---|---|
| Burning wire flammability index | 3.0mm | IEC 60695-2-12 | 650 °C |
| UL flame retardant rating | 1.0mm | UL 94 | HB |
| physical property | Test Condition | Test Method | SABIC INNOVATIVE SHANGHAI/PPX830 |
|---|---|---|---|
| Shrinkage rate | MD：3.20mm | 内部方法 | 0.20-0.25 % |
| melt mass-flow rate | 280°C/5.0kg | ASTM D1238 | 6.0 g/10min |
| Shrinkage rate | TD：3.20mm | 内部方法 | 0.40-0.60 % |
| Melt volume flow rate | 280°C/5.0kg | ISO 1133 | 6.00 cm3/10min |
| Thermal performance | Test Condition | Test Method | SABIC INNOVATIVE SHANGHAI/PPX830 |
|---|---|---|---|
| Heat distortion temperature | 0.45MPa,Unannealed,64.0mmSpan，HDT | ISO 75-2/Bf | 168 °C |
| vicat | ISO 306/B120 | 150 °C | |
| Linear coefficient of thermal expansion | TD：-40to95°C | ASTME831 | 1.3E-04 cm/cm/°C |
| MD：-40到95°C | ASTME831 | 2.5E-05 cm/cm/°C | |
| TD：-30to80°C | ISO 11359-2 | 1.2E-04 cm/cm/°C | |
| Heat distortion temperature | 0.45MPa,未退火,3.20mm，HDT | ASTM D648 | 166 °C |
| Linear coefficient of thermal expansion | MD：-30到80°C | ISO 11359-2 | 2.5E-05 cm/cm/°C |
| Heat distortion temperature | 1.8MPa,Unannealed,64.0mmSpan，HDT | ISO 75-2/Af | 153 °C |
| 1.8MPa,未退火,3.20mm，HDT | ASTM D648 | 156 °C | |
| ball-indentation hardness | 125°C | IEC 60695-10-2 | Pass |