PBT Cristin® S600F40 NC010 DUPONT USA
210
- Unit Price:US$ 4,052 /MT
- Packaging Specification:25 KG/PKG
- Packaging Material:Paper bag
- Supply Quantity:48MT
- Delivery Terms:FOB
- Port of Loading :China Main Port
- Accepted Payment Methods:T/T
- Shipping:Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 ********View
serv********View
For more details, please contact the supplier!
Material Description
- Material Properties:Low viscosity
- Application Areas:Electronic and electrical components
- Color:--
- Grade:Enhanced level
Material Certification
Technical Data Sheet
Compare
| thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| UL flame retardant rating | 3.00 mm | UL 94 | HB |
| 1.50 mm | UL 94 | HB | |
| 6.00 mm | UL 94 | HB | |
| melting temperature | ISO 11357-3 | 225 °C |
| flammability | Test Condition | Test Method | Test Result |
|---|---|---|---|
| burning rate | 1.00mm | ISO 3795 | 28 mm/min |
| UL flame retardant rating | 0.75mm | UL 94 | HB |
| 1.5mm | UL 94 | HB | |
| 0.75mm | IEC 60695-11-10,-20 | HB | |
| 1.5mm | IEC 60695-11-10,-20 | HB | |
| FMVSS flammability | FMVSS302 | B |
| Supplementary Information | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Odor | VDA270 | 3.00 |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Charpy Notched Impact Strength | 23°C | ISO 179/1eA | 4.5 kJ/m² |
| Impact strength of cantilever beam gap | 23°C | ISO 180/1A | 4.0 kJ/m² |
| Physical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| density | ISO 1183 | 1.31 g/cm | |
| Ejection Temperature | 170 °C | ||
| density | ISO 1183 | 1.31 g/cm³ | |
| melt mass-flow rate | 250°C/2.16kg | ISO 1133 | 33 g/10min |
| shrinkage rate | TD | ISO 294-4 | 1.8 % |
| MD | ISO 294-4 | 1.8 % |
| mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Tensile modulus | 0.00 mm, 23 ℃, Injection Molded | ISO 527-1 | 2600 MPa |
| bending strength | 0.00 mm, 23 ℃, 0.0 % | ISO 178 | 85 MPa |
| Tensile modulus | ISO 527-2 | 2600 Mpa | |
| tensile strength | 屈服 | ISO 527-2 | 58.0 Mpa |
| Tensile strain | 屈服 | ISO 527-2 | 4.0 % |
| Nominal tensile fracture strain | ISO 527-2 | 20 % | |
| bending strength | ISO 178 | 85.0 Mpa |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.