Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PBT S600F40 NC010 DUPONT USA
Cristin®
Electronic and electrical components
Low viscosity
UL
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | DUPONT USA/S600F40 NC010 |
|---|---|---|---|
| Charpy Notched Impact Strength | 23°C | ISO 179/1eA | 4.5 kJ/m² |
| Impact strength of cantilever beam gap | 23°C | ISO 180/1A | 4.0 kJ/m² |
| Supplementary Information | Test Condition | Test Method | DUPONT USA/S600F40 NC010 |
|---|---|---|---|
| Odor | VDA270 | 3.00 |
| thermal performance | Test Condition | Test Method | DUPONT USA/S600F40 NC010 |
|---|---|---|---|
| melting temperature | ISO 11357-3 | 225 °C | |
| UL flame retardant rating | 6.00 mm | UL 94 | HB |
| 1.50 mm | UL 94 | HB | |
| 3.00 mm | UL 94 | HB |
| mechanical properties | Test Condition | Test Method | DUPONT USA/S600F40 NC010 |
|---|---|---|---|
| bending strength | 0.00 mm, 23 ℃, 0.0 % | ISO 178 | 85 MPa |
| ISO 178 | 85.0 Mpa | ||
| Nominal tensile fracture strain | ISO 527-2 | 20 % | |
| Tensile modulus | ISO 527-2 | 2600 Mpa | |
| 0.00 mm, 23 ℃, Injection Molded | ISO 527-1 | 2600 MPa | |
| Tensile strain | 屈服 | ISO 527-2 | 4.0 % |
| tensile strength | 屈服 | ISO 527-2 | 58.0 Mpa |
| Physical properties | Test Condition | Test Method | DUPONT USA/S600F40 NC010 |
|---|---|---|---|
| density | ISO 1183 | 1.31 g/cm³ | |
| ISO 1183 | 1.31 g/cm | ||
| Ejection Temperature | 170 °C | ||
| melt mass-flow rate | 250°C/2.16kg | ISO 1133 | 33 g/10min |
| shrinkage rate | TD | ISO 294-4 | 1.8 % |
| MD | ISO 294-4 | 1.8 % |
| flammability | Test Condition | Test Method | DUPONT USA/S600F40 NC010 |
|---|---|---|---|
| burning rate | 1.00mm | ISO 3795 | 28 mm/min |
| FMVSS flammability | FMVSS302 | B | |
| UL flame retardant rating | 0.75mm | UL 94 | HB |
| 0.75mm | IEC 60695-11-10,-20 | HB | |
| 1.5mm | IEC 60695-11-10,-20 | HB | |
| 1.5mm | UL 94 | HB |