PA66 Leona™ FG170 BK ASAHI JAPAN

312

Unit Price:US$ 4,480 /MT
Packaging Specification:
25 KG/PKG
Packaging Material:
Paper bag
Supply Quantity:
77MT
Delivery Terms:
FOB
Port of Loading :
Guangzhou port, China
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View

serv********View

+86 ********View

For more details, please contact the supplier!

Material Description

Material Properties:Glass fiber reinforced｜Flame retardant
Application Areas:Electrical applications｜switch｜Hose
Color:--
Grade:Enhanced level

Material Certification

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result	Test Unit
Impact strength of simply supported beam without notch		ISO 179	44	kJ/m²
flammability	Test Condition	Test Method	Test Result	Test Unit
UL flame retardant rating	0.75 mm	UL 94	V-0
Burning wire flammability index	3.0 mm	IEC 60695-2-12	960	°C
Extreme Oxygen Index		ASTM D2863	38	%
mechanical properties	Test Condition	Test Method	Test Result	Test Unit
Taber abraser	1000 Cycles	ASTM D1044	--	mg
bending strength	23°C	ISO 178	188	Mpa
bending strength	bending strength	--	ASTM D790	191	Mpa
Bending modulus	23°C	ISO 178	7500	Mpa
Bending modulus	Bending modulus	--	ASTM D790	6400	Mpa
elongation	Break, 23°C	ISO 527-2	2.5	%
elongation	elongation	Break	ASTM D638	2.5	%
tensile strength	--	ASTM D638	132	Mpa
tensile strength	tensile strength	Break, 23°C	ISO 527-2	131	Mpa
Tensile modulus	23°C	ISO 527-2	7500	Mpa
thermal performance	Test Condition	Test Method	Test Result	Test Unit
Linear coefficient of thermal expansion	Flow	ASTM D696	3.0E-5	cm/cm/°C
Hot deformation temperature	1.8 MPa, Unannealed	ISO 75-2/A	240	°C
	Hot deformation temperature	1.8 MPa, Unannealed	ASTM D648	248	°C
		Hot deformation temperature	0.45 MPa, Unannealed	ISO 75-2/B	256	°C
		Hot deformation temperature	Hot deformation temperature	0.45 MPa, Unannealed	ASTM D648	255	°C
Physical properties	Test Condition	Test Method	Test Result	Test Unit
Water absorption rate	Equilibrium, 23°C, 50% RH	ISO 62	--	%
Water absorption rate	Water absorption rate	Saturation, 23°C		--	%
Shrinkage rate	Flow	Internal Method	0.60	%
Shrinkage rate	Shrinkage rate	横向Flow	Internal Method	1.0	%
Electrical performance	Test Condition	Test Method	Test Result	Test Unit
Volume resistivity	23°C	IEC 60093	1.0E+15	ohms·cm
Dielectric strength		ASTM D149	27	KV/mm
Compared to the anti leakage trace index	3.00 mm	IEC 60112	PLC 3
Volume resistivity	--	ASTM D257	1.0E+15	ohms·cm
Surface resistivity		ASTM D257	1.0E+14	ohms
hardness	Test Condition	Test Method	Test Result	Test Unit
Rockwell hardness	M -Sale	ISO 2039-2	95
Rockwell hardness	Rockwell hardness	M-Scale	ASTM D785	95

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.

Supplier Join

Get App

Top

PA66 Leona™ FG170 BK ASAHI JAPAN

Material Description

Material Certification

Technical Data Sheet

Sourcing & Prices

Selling & Verification

Explore Materials

Price Index