Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PA66 FG170 BK ASAHI JAPAN
Leona™
Electrical applications、switch、Hose
Glass fiber reinforced、Flame retardant
UL
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | ASAHI JAPAN/FG170 BK |
|---|---|---|---|
| Impact strength of simply supported beam without notch | ISO 179 | 44 kJ/m² |
| hardness | Test Condition | Test Method | ASAHI JAPAN/FG170 BK |
|---|---|---|---|
| Rockwell hardness | M 级 | ASTM D785 | 95 |
| M 计秤 | ISO 2039-2 | 95 |
| Mechanical properties | Test Condition | Test Method | ASAHI JAPAN/FG170 BK |
|---|---|---|---|
| tensile strength | 断裂, 23°C | ISO 527-2 | 131 Mpa |
| Taber abraser | 1000 Cycles | ASTM D1044 | -- mg |
| elongation | 断裂 | ASTM D638 | 2.5 % |
| tensile strength | -- | ASTM D638 | 132 Mpa |
| elongation | 断裂, 23°C | ISO 527-2 | 2.5 % |
| bending strength | -- | ASTM D790 | 191 Mpa |
| 23°C | ISO 178 | 188 Mpa | |
| Flexural modulus | 23°C | ISO 178 | 7500 Mpa |
| Tensile modulus | 23°C | ISO 527-2 | 7500 Mpa |
| Flexural modulus | -- | ASTM D790 | 6400 Mpa |
| Electrical performance | Test Condition | Test Method | ASAHI JAPAN/FG170 BK |
|---|---|---|---|
| Surface Resistivity | ASTM D257 | 1.0E+14 ohms | |
| Volume resistivity | -- | ASTM D257 | 1.0E+15 ohms·cm |
| Compared to the Leakage Tracking Index (CTI) | 3.00 mm | IEC 60112 | PLC 3 |
| Volume resistivity | 23°C | IEC 60093 | 1.0E+15 ohms·cm |
| dielectric strength | ASTM D149 | 27 KV/mm |
| flammability | Test Condition | Test Method | ASAHI JAPAN/FG170 BK |
|---|---|---|---|
| UL flame retardant rating | 0.75 mm | UL 94 | V-0 |
| Burning wire flammability index | 3.0 mm | IEC 60695-2-12 | 960 °C |
| Limiting Oxygen Index | ASTM D2863 | 38 % |
| physical property | Test Condition | Test Method | ASAHI JAPAN/FG170 BK |
|---|---|---|---|
| Water absorption rate | 平衡, 23°C, 50% RH | ISO 62 | -- % |
| Shrinkage rate | 横向流量 | 内部方法 | 1.0 % |
| Water absorption rate | 饱和, 23°C | -- % | |
| Shrinkage rate | 流量 | 内部方法 | 0.60 % |
| Thermal performance | Test Condition | Test Method | ASAHI JAPAN/FG170 BK |
|---|---|---|---|
| Heat distortion temperature | 0.45 MPa, 未退火，HDT | ISO 75-2/B | 256 °C |
| 0.45 MPa, 未退火，HDT | ASTM D648 | 255 °C | |
| 1.8 MPa, 未退火，HDT | ISO 75-2/A | 240 °C | |
| 1.8 MPa, 未退火，HDT | ASTM D648 | 248 °C | |
| Linear coefficient of thermal expansion | 流动 | ASTM D696 | 3.0E-5 cm/cm/°C |