ASA/PC GELOY™ HRA170-BR6A1436 SABIC INNOVATIVE US
417
- Unit Price:US$ 2,818 /MT
- Packaging Specification:25 KG/PKG
- Packaging Material:Paper bag
- Supply Quantity:80MT
- Delivery Terms:FOB
- Port of Loading :China Main Port
- Accepted Payment Methods:T/T
- Shipping:Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 ********View
serv********View
For more details, please contact the supplier!
Material Description
- Material Properties:Weather resistance｜heat-resisting｜High impact resistance
- Application Areas:Automotive sector
- Color:--
- Grade:Injection grade
Technical Data Sheet
| hardness | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Rockwell hardness | R -Sale | ISO 2039-2 | 120 |
| Ball Pressure Test | H 358/30 | ISO 2039-1 | 106 Mpa |
| thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Hot deformation temperature | 0.45 MPa, Unannealed, 4.00 mm, 100 mm Span | ISO 75-2/Be | 121 °C |
| 1.8 MPa, Unannealed, 4.00 mm, 100 mm Span | ISO 75-2/Ae | 112 °C | |
| Vicat softening temperature | -- | ISO 306/B50 | 129 °C |
| -- | ISO 306/B120 | 132 °C | |
| Linear coefficient of thermal expansion | 23 to 60°C，Flow | ISO 11359-2 | 8.0E-5 cm/cm/°C |
| thermal conductivity | ISO 8302 | 0.20 W/m/K |
| flammability | Test Condition | Test Method | Test Result |
|---|---|---|---|
| UL flame retardant rating | 1.6 mm | UL 94 | HB |
| Burning wire flammability index | 3.2 mm | IEC 60695-2-12 | 750 °C |
| Extreme Oxygen Index | ISO 4589-2 | 22 % |
| Physical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Melt Volume Flow Rate (MVR) | 260°C/5.0 kg | ISO 1133 | 17.0 cm3/10min |
| Shrinkage rate | Flow | Internal Method | 0.40 - 0.60 % |
| Water absorption rate | Saturation, 23°C | ISO 62 | 0.60 % |
| Equilibrium, 23°C, 50% RH | ISO 62 | 0.20 % |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Surface resistivity | IEC 60093 | > 1.0E+15 ohms | |
| Volume resistivity | IEC 60093 | > 1.0E+15 ohms·cm | |
| Dielectric strength | 3.20 mm, in Oil | IEC 60243-1 | 17 KV/mm |
| Relative permittivity | 1 MHz | IEC 60250 | 2.80 |
| Dissipation factor | 1 MHz | IEC 60250 | 0.013 |
| Compared to the anti leakage trace index | IEC 60112 | V |
| injection | Test Condition | Test Method | Test Result |
|---|---|---|---|
| drying temperature | 100 to 110 °C | ||
| drying time | 2.0 to 4.0 hr | ||
| Suggested maximum moisture content | 0.020 % | ||
| Hopper temperature | 60 to 80 °C | ||
| Temperature at the rear of the barrel | 230 to 260 °C | ||
| Temperature in the middle of the barrel | 250 to 290 °C | ||
| Temperature at the front of the material cylinder | 250 to 290 °C | ||
| Spray nozzle temperature | 240 to 280 °C | ||
| Processing (melt) temperature | 260 to 290 °C | ||
| Mold temperature | 60 to 90 °C |
| mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Tensile modulus | ISO 527-2/1 | 2500 Mpa | |
| tensile strength | Yield | ISO 527-2/5 | 55.0 Mpa |
| Yield | ISO 527-2/50 | 62.0 Mpa | |
| Break | ISO 527-2/5 | 60.0 Mpa | |
| Break | ISO 527-2/50 | 62.0 Mpa | |
| Tensile strain | Yield | ISO 527-2/5 | 5.0 % |
| Yield | ISO 527-2/50 | 4.0 % | |
| Break | ISO 527-2/5 | 130 % | |
| Break | ISO 527-2/50 | > 50 % | |
| Bending modulus | ISO 178 | 2400 Mpa | |
| bending strength | ISO 178 | 85.0 Mpa | |
| Taber abraser | 1000 Cycles, 1000 g, CS-17 Wheel | Internal Method | 95.0 mg |
| impact performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Charpy Notched Impact Strength | -30°C | ISO 179/1eA | 12 kJ/m² |
| 23°C | ISO 179/1eA | 60 kJ/m² | |
| Impact strength of cantilever beam gap | -30°C | ISO 180/1A | 15 kJ/m² |
| 23°C | ISO 180/1A | 45 kJ/m² |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.