ABS MAGNUM™ 8391 STYRON US

405

Unit Price:US$ 2,580 /MT
Packaging Specification:
25 KG/PKG
Packaging Material:
Paper bag
Supply Quantity:
20MT
Delivery Terms:
FOB
Port of Loading :
Guangzhou port, China
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View

serv********View

+86 ********View

For more details, please contact the supplier!

Material Description

Material Properties:High mobility｜High gloss｜heat-resisting
Application Areas:Household appliances｜Fitness equipment｜Toy
Color:--
Grade:Heat resistant grade

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result	Test Unit
Charpy Notched Impact Strength	-30°C	ISO 179/1eU2	NoBreak
	Charpy Notched Impact Strength	23°C	ISO 179/1eU2	NoBreak
	Charpy Notched Impact Strength	Charpy Notched Impact Strength	23°C	ISO 179/1eA2	18.0	kJ/m²
flammability	Test Condition	Test Method	Test Result	Test Unit
Burning rate	2.00mm	ISO 3795	60	mm/min
UL flame retardant rating	1.5mm	UL 94	HB
UL flame retardant rating	UL flame retardant rating	3.0mm	UL 94	HB
Normal combustion performance with a thickness of 1.6mm	1.50mm,UL		HB	4.21
mechanical properties	Test Condition	Test Method	Test Result	Test Unit
bending strength	3.20mm,InjectionMolded	ISO 178	70.0	Mpa
bending strength	bending strength		ASTM D790	75.0	Mpa
Bending modulus	3.20mm,InjectionMolded	ISO 178	2400	Mpa
Bending modulus	Bending modulus		ASTM D790	2480	Mpa
Nominal fracture strain		ISO 527-22	20	%
elongation	Break	ASTM D638	8.7	%
Tensile strain	Yield,3.20mm,Injection	ISO 527-2/100	2.6	%
Tensile strain	Tensile strain	Yield,3.20mm,Injection	ISO 527-2/50	2.5	%
elongation	Yield	ASTM D638	2.7	%
tensile strength	Break	ASTM D638	35.0	Mpa
	tensile strength	Yield	ISO 527-22	48.0	Mpa
		tensile strength	Yield,3.20mm,Injection	ISO 527-2/100	47.0	Mpa
			tensile strength	Yield,3.20mm,Injection	ISO 527-2/50	45.0	Mpa
			tensile strength	tensile strength	Yield	ASTM D638	48.0	Mpa
Tensile modulus		ISO 527-22	2400	Mpa
Tensile modulus	Tensile modulus	3.20mm,Injection	ISO 527-2	2340	Mpa
thermal performance	Test Condition	Test Method	Test Result	Test Unit
Vicat softening temperature		ISO 306/B50	95.0	°C
	Vicat softening temperature	50N	ISO 3062	92.0	°C
	Vicat softening temperature	Vicat softening temperature		ASTM D15257	99.0	°C
Hot deformation temperature	1.8MPa	ISO 75-22	95.0	°C
	Hot deformation temperature	1.8MPa,Annealed	ISO 75-2/A	95.0	°C
		Hot deformation temperature	1.8MPa,Unannealed	ASTM D648	74.0	°C
		Hot deformation temperature	Hot deformation temperature	0.45MPa,Unannealed	ASTM D648	87.0	°C
Physical properties	Test Condition	Test Method	Test Result	Test Unit
Apparent density		ISO 60	0.65	g/cm³
melt mass-flow rate	220°C/10.0kg	ASTM D1238	28	g/10min
	melt mass-flow rate	230°C/3.8kg	ASTM D1238	8.0	g/10min
	melt mass-flow rate	melt mass-flow rate	220°C/10.0kg	ISO 1133	28	g/10min
Melt Volume Flow Rate (MVR)	220°C/10.0kg	ASTM D1505	27.0	cm3/10min
Shrinkage rate	MD	ASTM D955	0.40-0.70	%
Shrinkage rate	Shrinkage rate	MD	ISO 294-4	0.40-0.70	%
hardness	Test Condition	Test Method	Test Result	Test Unit
Rockwell hardness	R-Scale	ASTM D785	108

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.

Supplier Join

Get App

Top

ABS MAGNUM™ 8391 STYRON US

Material Description

Technical Data Sheet

Sourcing & Prices

Selling & Verification

Explore Materials

Price Index