Material Description
- Material Properties:Flame retardant｜Glass fiber reinforced｜Mineral reinforcement｜High rigidity｜high strength｜High temperature resistance
- Application Areas:Fiber grade
- Color:--
- Grade:Flame retardant enhanced grade
Material Certification
Technical Data Sheet
Compare
| physical property | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Water absorption rate | ISO 62 | 0.02 % | |
| Shrinkage rate | 东丽法 | 0.15 % | |
| 东丽法 | 0.55 % | ||
| 东丽法 | 90 |
| hardness | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Rockwell hardness | ISO 2039-2 | 123 R |
| other | Test Condition | Test Method | Test Result |
|---|---|---|---|
| characteristic | 标准 | ||
| Color | 本色.黑 |
| flammability | Test Condition | Test Method | Test Result |
|---|---|---|---|
| UL flame retardant rating | UL -94 | V-0 0.36mm | |
| UL -94 | V-0 0.74mm | ||
| UL -94 | V-0 1.50mm | ||
| UL -94 | V-0 3.00mm | ||
| UL -94 | V-0.5VA 2.00mm |
| Basic performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Water absorption rate | ASTM D-570 | 0.02 % |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Charpy Notched Impact Strength | ASTM D256/ISO 179 | 8 kg·cm/cm(J/M)ft·lb/in | |
| ASTM D256/ISO 179 | 18 kg·cm/cm(J/M)ft·lb/in | ||
| elongation at break | ASTM D638/ISO 527 | 0.8 % | |
| tensile strength | ASTM D638/ISO 527 | 130 kg/cm²(MPa)[Lb/in²] | |
| Rockwell hardness | ASTM D785 | 123 | |
| Flexural modulus | ASTM D790/ISO 178 | 22 kg/cm²(MPa)[Lb/in²] | |
| bending strength | ASTM D790/ISO 178 | 210 kg/cm²(MPa)[Lb/in²] | |
| elongation at break | ISO 527-2 | 0.8 % | |
| bending strength | ISO 178 | 210 Mpa | |
| Flexural modulus | ISO 178 | 22000 Mpa | |
| shear strength | ISO 178 | 60 Mpa | |
| Charpy Notched Impact Strength | ISO 179/1eA | 8.0 kJ/m² | |
| Impact strength of simply supported beam without notch | ISO 179/1eU | 18 kJ/m² | |
| tensile strength | ISO 527-2 | 130 Mpa | |
| bending strength | ASTM D-790 | 200 Mpa | |
| elongation at break | ASTM D-732 | 60 | |
| limiting pv value | 东丽法 | 815 KJ/m | |
| Impact strength of cantilever beam gap | ASTM D-256 | 90 J/m | |
| ASTM D-256 | 20 KJ/m | ||
| abrasion | ASTM D-1044 | 70 mg/1000回 | |
| tensile strength | ASTM D-638 | 140 Mpa | |
| coefficient of friction | ASTM D-1894 | 0.30 | |
| tensile strength | ASTM D-638 | 1.2 % | |
| Shore hardness | ASTM D-785 | 123 洛氏 | |
| bending strength | ASTM D-790 | 17.6 GPa |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| dielectric constant | ASTM D150/IEC 60250 | 5 | |
| Volume resistivity | ASTM D257/IEC 60093 | 1014 Ω.cm | |
| IEC 60093 | 1E+19 Ω.cm | ||
| dielectric strength | IEC 60243-1 | 19 KV/mm | |
| dielectric constant | IEC 60250 | 5.1 1MHz | |
| Dissipation Factor | IEC 60250 | 2E-03 1MHz | |
| dielectric strength | ASTM D-149 | 15 MV/m | |
| Inherent resistance of volume | ASTM D-257 | 10 Ω.m | |
| arc resistance | ASTM D-495 | 182 秒 | |
| Induced positive connection | ASTM D-150 | 0.002 | |
| dielectric constant | ASTM D-150 | 5.8 |
| Physical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| density | ASTM D792/ISO 1183 | 1.97 | |
| Shrinkage rate | ASTM D955 | 0.2 % | |
| Water absorption rate | ASTM D570/ISO 62 | 0.02 % |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Combustibility (rate) | UL 94 | V-0 | |
| Heat distortion temperature | ASTM D648/ISO 75 | >260 ℃（℉） | |
| melting temperature | 278 ℃（℉） | ||
| Linear coefficient of thermal expansion | ASTM D696/ISO 11359 | 1.7 mm/mm.℃ | |
| Heat distortion temperature | ISO 75-2/Af | >260 °C | |
| vicat | ISO 11357-3 | 278 °C | |
| Linear coefficient of thermal expansion | ISO 11359-2 | 1.7E-05 cm/cm/°C | |
| ISO 11359-2 | 2.4E-05 cm/cm/°C | ||
| Heat distortion temperature | ASTM D-648 | >260 °C | |
| Linear coefficient of thermal expansion | ASTM D-696 | 1.6 | |
| ASTM D-696 | 2.4 | ||
| melting temperature | DSC | 278 °C | |
| combustibility | UL -94 | V-0 |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.