Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PPS A310MX04 TORAY JAPAN
Torelina®
Fiber grade
Flame retardant、Glass fiber reinforced、Mineral reinforcement、High rigidity、high strength、High temperature resistan
UL
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| hardness | Test Condition | Test Method | TORAY JAPAN/A310MX04 |
|---|---|---|---|
| Rockwell hardness | ISO 2039-2 | 123 R |
| Basic performance | Test Condition | Test Method | TORAY JAPAN/A310MX04 |
|---|---|---|---|
| Water absorption rate | ASTM D-570 | 0.02 % |
| Electrical performance | Test Condition | Test Method | TORAY JAPAN/A310MX04 |
|---|---|---|---|
| dielectric strength | IEC 60243-1 | 19 KV/mm | |
| ASTM D-149 | 15 MV/m | ||
| dielectric constant | ASTM D150/IEC 60250 | 5 | |
| 23°C | IEC 60250 | 5.1 1MHz | |
| Induced positive connection | 10 | ASTM D-150 | 0.002 |
| Dissipation Factor | 23°C | IEC 60250 | 2E-03 1MHz |
| Inherent resistance of volume | ASTM D-257 | 10 Ω.m | |
| arc resistance | W电极 | ASTM D-495 | 182 秒 |
| Volume resistivity | ASTM D257/IEC 60093 | 1014 Ω.cm | |
| dielectric constant | 10 | ASTM D-150 | 5.8 |
| Volume resistivity | IEC 60093 | 1E+19 Ω.cm |
| Mechanical properties | Test Condition | Test Method | TORAY JAPAN/A310MX04 |
|---|---|---|---|
| bending strength | ASTM D790/ISO 178 | 210 kg/cm²(MPa)[Lb/in²] | |
| Flexural modulus | ASTM D790/ISO 178 | 22 kg/cm²(MPa)[Lb/in²] | |
| Shore hardness | ASTM D-785 | 123 洛氏 | |
| Charpy Notched Impact Strength | 23°C | ISO 179/1eA | 8.0 kJ/m² |
| coefficient of friction | 对钢 | ASTM D-1894 | 0.30 |
| Impact strength of cantilever beam gap | 无缺口23℃ | ASTM D-256 | 20 KJ/m |
| bending strength | ASTM D-790 | 200 Mpa | |
| abrasion | ASTM D-1044 | 70 mg/1000回 | |
| elongation at break | ASTM D638/ISO 527 | 0.8 % | |
| tensile strength | ASTM D-638 | 140 Mpa | |
| Rockwell hardness | ASTM D785 | 123 | |
| limiting pv value | 东丽法 | 815 KJ/m | |
| tensile strength | ASTM D638/ISO 527 | 130 kg/cm²(MPa)[Lb/in²] | |
| Impact strength of simply supported beam without notch | 23°C | ISO 179/1eU | 18 kJ/m² |
| bending strength | ASTM D-790 | 17.6 GPa | |
| shear strength | ISO 178 | 60 Mpa | |
| bending strength | 23°C | ISO 178 | 210 Mpa |
| Impact strength of cantilever beam gap | 缺口23℃ | ASTM D-256 | 90 J/m |
| elongation at break | ASTM D-732 | 60 | |
| tensile strength | ASTM D-638 | 1.2 % | |
| Flexural modulus | 23°C | ISO 178 | 22000 Mpa |
| Charpy Notched Impact Strength | ASTM D256/ISO 179 | 18 kg·cm/cm(J/M)ft·lb/in | |
| elongation at break | 23°C | ISO 527-2 | 0.8 % |
| tensile strength | 23°C | ISO 527-2 | 130 Mpa |
| other | Test Condition | Test Method | TORAY JAPAN/A310MX04 |
|---|---|---|---|
| characteristic | 标准 | ||
| Color | 本色.黑 |
| Physical properties | Test Condition | Test Method | TORAY JAPAN/A310MX04 |
|---|---|---|---|
| Shrinkage rate | ASTM D955 | 0.2 % | |
| density | ASTM D792/ISO 1183 | 1.97 | |
| Water absorption rate | ASTM D570/ISO 62 | 0.02 % |
| flammability | Test Condition | Test Method | TORAY JAPAN/A310MX04 |
|---|---|---|---|
| UL flame retardant rating | UL -94 | V-0 0.74mm | |
| UL -94 | V-0.5VA 2.00mm | ||
| UL -94 | V-0 1.50mm | ||
| UL -94 | V-0 0.36mm | ||
| UL -94 | V-0 3.00mm |
| physical property | Test Condition | Test Method | TORAY JAPAN/A310MX04 |
|---|---|---|---|
| Water absorption rate | (23°C,24hr) | ISO 62 | 0.02 % |
| Shrinkage rate | 流动方向 | 东丽法 | 0.15 % |
| 320℃,98MPa,1mm厚，流动长 | 东丽法 | 90 | |
| Shrinkage rate | 垂重方向 | 东丽法 | 0.55 % |
| Thermal performance | Test Condition | Test Method | TORAY JAPAN/A310MX04 |
|---|---|---|---|
| Combustibility (rate) | UL 94 | V-0 | |
| combustibility | UL -94 | V-0 | |
| Linear coefficient of thermal expansion | 流动方向 | ASTM D-696 | 1.6 |
| ASTM D696/ISO 11359 | 1.7 mm/mm.℃ | ||
| Heat distortion temperature | 1.80MPa退火，HDT | ISO 75-2/Af | >260 °C |
| Linear coefficient of thermal expansion | 垂重方向 | ASTM D-696 | 2.4 |
| Heat distortion temperature | 1.82MPa，HDT | ASTM D-648 | >260 °C |
| HDT | ASTM D648/ISO 75 | >260 ℃（℉） | |
| vicat | 熔融温度 | ISO 11357-3 | 278 °C |
| Linear coefficient of thermal expansion | MD | ISO 11359-2 | 1.7E-05 cm/cm/°C |
| melting temperature | DSC | 278 °C | |
| 278 ℃（℉） | |||
| Linear coefficient of thermal expansion | TD | ISO 11359-2 | 2.4E-05 cm/cm/°C |