Material Description
- Material Properties:Flame retardant
- Application Areas:Electronic communication accessories｜Electronic communication accessories｜building materials｜Profile
- Color:--
- Grade:Injection grade
Technical Data Sheet
Compare
| physical property | Test Condition | Test Method | Test Result |
|---|---|---|---|
| melt mass-flow rate | ASTM D1238 | 3.9 g/10 min | |
| Melt volume flow rate | ISO 1133 | 27.0 cm3/10min | |
| ISO 1133 | 10.0 cm3/10min | ||
| ISO 1133 | 23.0 cm3/10min | ||
| Shrinkage rate | 内部方法 | 0.50 - 0.70 % | |
| Water absorption rate | ASTM D570 | 0.070 % |
| flammability | Test Condition | Test Method | Test Result |
|---|---|---|---|
| UL flame retardant rating | UL 94 | V-2 | |
| UL 94 | V-0 | ||
| UL 94 | 5VA |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| tensile strength | 内部方法 | 63.0 Mpa | |
| ISO 527-2/50 | 73.0 Mpa | ||
| Tensile strain | 内部方法 | 85 % | |
| ISO 527-2/50 | 4.5 % | ||
| Flexural modulus | ASTM D790 | 2350 Mpa | |
| ISO 178 | 2600 Mpa | ||
| bending strength | ASTM D790 | 99.0 Mpa | |
| ISO 178 | 108 Mpa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Impact strength of simply supported beam without notch | ISO 179/1eU | 9.0 kJ/m² |
| Filling analysis | Test Condition | Test Method | Test Result |
|---|---|---|---|
| melt viscosity | ISO 11443 | 278 Pa·s |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Surface Resistivity | ASTM D257 | 1.0E+16 ohms | |
| dielectric constant | ASTM D150 | 2.80 | |
| ASTM D150 | 2.80 |
| injection | Test Condition | Test Method | Test Result |
|---|---|---|---|
| drying temperature | 105 to 110 °C | ||
| drying time | 3.0 to 4.0 hr | ||
| Suggested maximum moisture content | 0.020 % | ||
| Suggested injection volume | 30 to 70 % | ||
| Temperature at the rear of the barrel | 245 to 295 °C | ||
| Temperature in the middle of the barrel | 255 to 300 °C | ||
| Temperature at the front of the material cylinder | 265 to 305 °C | ||
| Spray nozzle temperature | 275 to 305 °C | ||
| Processing (melt) temperature | 275 to 305 °C | ||
| Temperature | 70 to 100 °C | ||
| Back pressure | 0.300 to 0.700 Mpa | ||
| screw speed | 20 to 100 rpm | ||
| Exhaust hole depth | 0.038 to 0.051 mm |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Heat distortion temperature | ASTM D648 | 136 °C | |
| ASTM D648 | 125 °C | ||
| ISO 75-2/Af | 117 °C | ||
| vicat | ISO 306/A120 | 151 °C | |
| ISO 306/B120 | 142 °C | ||
| ball-indentation hardness | IEC 60695-10-2 | 通过 | |
| Linear coefficient of thermal expansion | TMA | 7.0E-5 cm/cm/°C | |
| ISO 11359-2 | 6.6E-5 cm/cm/°C | ||
| ISO 11359-2 | 7.6E-5 cm/cm/°C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.