PPO PX9406P-701 SABIC INNOVATIVE SHANGHAI

FLEX NORYL™

Electronic communication accessories,Electronic communication accessories,building materials,Profile

Flame retardant

--

--

--

--

--

--

--

--

--

--

--

--

--

--

--

Plastic Datasheets

thermal performance	Test Condition	Test Method	SABIC INNOVATIVE SHANGHAI/PX9406P-701
Ball Pressure Test	125°C	IEC 60695-10-2	通过
Hot deformation temperature	0.45 MPa, 未退火, 6.40 mm	ASTM D648	136 °C
		1.8 MPa, 未退火, 4.00 mm, 64.0 mm 跨距5	ISO 75-2/Af	117 °C
		1.8 MPa, 未退火, 6.40 mm	ASTM D648	125 °C
Linear coefficient of thermal expansion	横向 : -40°C	ISO 11359-2	7.6E-5 cm/cm/°C
		流动 : -40 到 40°C	ISO 11359-2	6.6E-5 cm/cm/°C
		流动 : -30 到 30°C	TMA	7.0E-5 cm/cm/°C
Vicat softening temperature	--	ISO 306/A120	151 °C
Vicat softening temperature		--	ISO 306/B120	142 °C

mechanical properties	Test Condition	Test Method	SABIC INNOVATIVE SHANGHAI/PX9406P-701
Bending modulus	--2	ISO 178	2600 Mpa
Bending modulus		--	ASTM D790	2350 Mpa
bending strength	--	ASTM D790	99.0 Mpa
bending strength		--2,3	ISO 178	108 Mpa
Tensile strain	断裂	Internal Method	85 %
Tensile strain		断裂	ISO 527-2/50	4.5 %
tensile strength	屈服	ISO 527-2/50	73.0 Mpa
tensile strength		屈服	Internal Method	63.0 Mpa

Electrical performance	Test Condition	Test Method	SABIC INNOVATIVE SHANGHAI/PX9406P-701
Dielectric constant	50 kHz	ASTM D150	2.80
Dielectric constant		60 Hz	ASTM D150	2.80
Surface resistivity		ASTM D257	1.0E+16 ohms

Physical properties	Test Condition	Test Method	SABIC INNOVATIVE SHANGHAI/PX9406P-701
melt mass-flow rate	250°C/10.0 kg	ASTM D1238	3.9 g/10 min
Melt Volume Flow Rate (MVR)	280°C/5.0 kg	ISO 1133	10.0 cm3/10min
		280°C/10.0 kg	ISO 1133	27.0 cm3/10min
		300°C/5.0 kg	ISO 1133	23.0 cm3/10min
Shrinkage rate	3.20 mm，Flow	Internal Method	0.50 - 0.70 %
Water absorption rate	24 hr	ASTM D570	0.070 %

impact performance	Test Condition	Test Method	SABIC INNOVATIVE SHANGHAI/PX9406P-701
Impact strength of simply supported beam without notch	-30°C	ISO 179/1eU	9.0 kJ/m²

flammability	Test Condition	Test Method	SABIC INNOVATIVE SHANGHAI/PX9406P-701
UL flame retardant rating	2.5 mm	UL 94	5VA
		0.75 mm	UL 94	V-0
		0.40 mm	UL 94	V-2

Filling analysis	Test Condition	Test Method	SABIC INNOVATIVE SHANGHAI/PX9406P-701
Melt viscosity	280°C, 1500 sec^-1	ISO 11443	278 Pa·s

injection	Test Condition	Test Method	SABIC INNOVATIVE SHANGHAI/PX9406P-701
Back pressure			0.300 to 0.700 Mpa
drying temperature			105 to 110 °C
drying time			3.0 to 4.0 hr
Exhaust hole depth			0.038 to 0.051 mm
Mold temperature			70 to 100 °C
Processing (melt) temperature			275 to 305 °C
Screw speed			20 to 100 rpm
Spray nozzle temperature			275 to 305 °C
Suggested injection volume			30 to 70 %
Suggested maximum moisture content			0.020 %
Temperature at the front of the material cylinder			265 to 305 °C
Temperature at the rear of the barrel			245 to 295 °C
Temperature in the middle of the barrel			255 to 300 °C