PBT Toraycon® 5107G TORAY JAPAN
190
- Unit Price:US$ 2,933 /MT
- Packaging Specification:25 KG/PKG
- Packaging Material:Paper bag
- Supply Quantity:45MT
- Delivery Terms:FOB
- Port of Loading :China Main Port
- Accepted Payment Methods:T/T
- Shipping:Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 ********View
serv********View
For more details, please contact the supplier!
Material Description
- Material Properties:High impact resistance｜Fast forming cycle
- Application Areas:Automotive sector
- Color:--
- Grade:Enhanced level
Technical Data Sheet
Compare
| thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Heat Deflection Temperature | 1.8 MPa, 未退火 | ISO 75-2/A | 208 °C |
| Linear coefficient of thermal expansion | -30 到 100℃ | ISO 11359-2 | 0.000042 cm/cm/℃ |
| UL flame retardant rating | UL 94 | HB | |
| Heat Deflection Temperature | 1.8MPa,未退火 | ISO 75-2/A | 208 °C |
| Linear coefficient of thermal expansion | MD：-30到100°C | ISO 11359-2 | 4.2E-05 cm/cm/°C |
| flammability | Test Condition | Test Method | Test Result |
|---|---|---|---|
| UL flame retardant rating | UL 94 | HB |
| Supplementary Information | Test Condition | Test Method | Test Result |
|---|---|---|---|
| BarFlowLength | 250°C,1.00mm | 内部方法 | 7.00 CM |
| Physical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| shrinkage rate | TD: 3.00 mm | 内部方法 | 1.0 % |
| MD: 3.00 mm | 内部方法 | 0.40 % | |
| Water absorption rate | 23℃, 24 hr | ISO 62 | 0.080 % |
| Flow Length | 250℃, 1.00 mm | 内部方法 | 7.00 CM |
| shrinkage rate | TD:3.00mm2 | 内部方法 | 1.0 % |
| MD:3.00mm4 | 内部方法 | 0.40 % | |
| Water absorption rate | 23°C,24hr | ISO 62 | 0.080 % |
| mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| bending strength | 23℃ | ISO 178 | 195 Mpa |
| Charpy Notched Impact Strength | 23℃ | ISO 179 | 12 kJ/m² |
| Tensile modulus | 23℃ | ISO 527-2 | 8400 Mpa |
| tensile strength | 屈服, 23℃ | ISO 527-2 | 125 Mpa |
| Tensile strain | 断裂, 23℃ | ISO 527-2 | 3.0 % |
| flexural modulus | 23℃ | ISO 178 | 7900 Mpa |
| Tensile modulus | 23°C | ISO 527-2 | 8400 Mpa |
| tensile strength | 屈服,23°C | ISO 527-2 | 125 Mpa |
| Tensile strain | 断裂,23°C | ISO 527-2 | 3.0 % |
| flexural modulus | 23°C | ISO 178 | 7900 Mpa |
| bending strength | 23°C | ISO 178 | 195 Mpa |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.