Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PBT 5107G TORAY JAPAN
Toraycon®
Automotive sector
High impact resistance,Fast forming cycle
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Supplementary Information | Test Condition | Test Method | TORAY JAPAN/5107G |
|---|---|---|---|
| BarFlowLength | 250°C,1.00mm | 内部方法 | 7.00 CM |
| Mechanical properties | Test Condition | Test Method | TORAY JAPAN/5107G |
|---|---|---|---|
| Tensile strain | 断裂,23°C | ISO 527-2 | 3.0 % |
| bending strength | 23°C | ISO 178 | 195 Mpa |
| Flexural modulus | 23℃ | ISO 178 | 7900 Mpa |
| tensile strength | 屈服,23°C | ISO 527-2 | 125 Mpa |
| Flexural modulus | 23°C | ISO 178 | 7900 Mpa |
| Tensile modulus | 23°C | ISO 527-2 | 8400 Mpa |
| tensile strength | 屈服, 23℃ | ISO 527-2 | 125 Mpa |
| Charpy Notched Impact Strength | 23℃ | ISO 179 | 12 kJ/m² |
| Tensile modulus | 23℃ | ISO 527-2 | 8400 Mpa |
| Tensile strain | 断裂, 23℃ | ISO 527-2 | 3.0 % |
| bending strength | 23℃ | ISO 178 | 195 Mpa |
| flammability | Test Condition | Test Method | TORAY JAPAN/5107G |
|---|---|---|---|
| UL flame retardant rating | UL 94 | HB |
| physical property | Test Condition | Test Method | TORAY JAPAN/5107G |
|---|---|---|---|
| Flow Length | 250℃, 1.00 mm | 内部方法 | 7.00 CM |
| Shrinkage rate | TD:3.00mm2 | 内部方法 | 1.0 % |
| MD:3.00mm4 | 内部方法 | 0.40 % | |
| MD: 3.00 mm | 内部方法 | 0.40 % | |
| Water absorption rate | 23°C,24hr | ISO 62 | 0.080 % |
| 23℃, 24 hr | ISO 62 | 0.080 % | |
| Shrinkage rate | TD: 3.00 mm | 内部方法 | 1.0 % |
| Thermal performance | Test Condition | Test Method | TORAY JAPAN/5107G |
|---|---|---|---|
| Linear coefficient of thermal expansion | -30 到 100℃ | ISO 11359-2 | 0.000042 cm/cm/℃ |
| Heat distortion temperature | 1.8 MPa, 未退火，HDT | ISO 75-2/A | 208 °C |
| 1.8MPa,未退火，HDT | ISO 75-2/A | 208 °C | |
| Linear coefficient of thermal expansion | MD：-30到100°C | ISO 11359-2 | 4.2E-05 cm/cm/°C |
| UL flame retardant rating | UL 94 | HB |