PA6 Zytel® 73G30L NC010 DUPONT USA
360
- Unit Price:US$ 1,785 /MT
- Packaging Specification:25 KG/PKG
- Packaging Material:Paper bag
- Supply Quantity:22MT
- Delivery Terms:FOB
- Port of Loading :China Main Port
- Accepted Payment Methods:T/T
- Shipping:Negotiate supplier for shipping details
- Material Comparison:
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 ********View
serv********View
+86 ********View
For more details, please contact the supplier!
Material Description
- Material Properties:High temperature resistance|enhance
- Application Areas:Electronic appliances|Wear resistant accessories|Home appliance accessories
- Color:--
- Grade:Injection grade
Material Certification

Technical Data Sheet
impact performance | Test Condition | Test Method | Test Result |
---|---|---|---|
Impact strength of simply supported beam without notch | -30°C | ISO 179/1eU | 80 kJ/m² |
23°C | ISO 179/1eU | 90 kJ/m² | |
Suspended wall beam without notch impact strength | -30°C | ISO 180/1U | 90 kJ/m² |
23°C | ISO 180/1U | 100 kJ/m² |
flammability | Test Condition | Test Method | Test Result |
---|---|---|---|
Burning rate | 1.00mm | ISO 3795 | 25 mm/min |
UL flame retardant rating | 1.5mm | UL 94 | HB |
3.0mm | UL 94 | HB | |
1.5mm | IEC 60695-11-10,-20 | HB | |
3.0mm | IEC 60695-11-10,-20 | HB | |
Extreme Oxygen Index | ISO 4589-2 | 21 % | |
FMVSS flammability | FMVSS302 | B | |
Atomization | F-value(refraction) | ISO 6452 | 95 % |
G-value(condensate) | ISO 6452 | 1E-04 g |
mechanical properties | Test Condition | Test Method | Test Result |
---|---|---|---|
Tensile modulus | ISO 527-2 | 10000 Mpa | |
tensile strength | Break | ISO 527-2 | 180 Mpa |
Tensile strain | Break | ISO 527-2 | 3.5 % |
Tensile creep modulus | 1hr | ISO 899-1 | -- Mpa |
1000hr | ISO 899-1 | -- Mpa | |
Bending modulus | ISO 178 | 8500 Mpa | |
bending strength | ISO 178 | 240 Mpa | |
Compressive stress | ISO 604 | 160 Mpa | |
shear strength | ASTM D732 | 60.0 Mpa | |
Charpy Notched Impact Strength | ASTM D256/ISO 179 | 6 kg·cm/cm(J/M)ft·lb/in | |
Tensile modulus | ASTM D638/ISO 527 | 9100 kg/cm²(MPa)[Lb/in²] | |
Bending modulus | ASTM D790/ISO 178 | 9000 kg/cm²(MPa)[Lb/in²] |
thermal performance | Test Condition | Test Method | Test Result |
---|---|---|---|
Hot deformation temperature | 0.45MPa,Unannealed | ISO 75-2/B | 220 °C |
1.8MPa,Unannealed | ISO 75-2/A | 210 °C | |
Glass transition temperature | ISO 11357-2 | 60.0 °C | |
Melting temperature | ISO 11357-3 | 221 °C | |
Linear coefficient of thermal expansion | MD | ISO 11359-2 | 1.4E-05 cm/cm/°C |
TD | ISO 11359-2 | 1E-04 cm/cm/°C | |
Hot deformation temperature | HDT | ASTM D648/ISO 75 | 221 ℃(℉) |
HDT | ASTM D648/ISO 75 | 210 ℃(℉) | |
Melting temperature | 221 ℃(℉) | ||
Vicat softening temperature | ASTM D1525/ISO R306 | 215 ℃(℉) |
Physical properties | Test Condition | Test Method | Test Result |
---|---|---|---|
Shrinkage rate | TD | ISO 294-4 | 0.60 % |
MD | ISO 294-4 | 0.20 % | |
Water absorption rate | Saturation,23°C,2.00mm | ISO 62 | 6.3 % |
Equilibrium,23°C,2.00mm,50%RH | ISO 62 | 1.9 % | |
ASTM D570/ISO 62 | 1.8 % |
Electrical performance | Test Condition | Test Method | Test Result |
---|---|---|---|
Volume resistivity | IEC 60093 | 1E+14 ohms·cm | |
Relative permittivity | 100Hz | IEC 60250 | 3.80 |
Dissipation factor | 100Hz | IEC 60250 | 0.022 |
Compared to the anti leakage trace index | CTI | UL 746 | PLC 0 |
IEC 60112 | PLC 0 |
Supplementary Information | Test Condition | Test Method | Test Result |
---|---|---|---|
EmissionofOrganicCompounds | VDA277 | 8.50 µgC/g | |
Odor | VDA270 | 3.50 |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.