| Impact resistance | Test Condition | Test Method | DUPONT USA/73G30L NC010 |
|---|---|---|---|
| Suspended wall beam without notch impact strength | -30°C | ISO 180/1U | 90 kJ/m² |
| 23°C | ISO 180/1U | 100 kJ/m² | |
| Impact strength of simply supported beam without notch | 23°C | ISO 179/1eU | 90 kJ/m² |
| -30°C | ISO 179/1eU | 80 kJ/m² |
| Supplementary Information | Test Condition | Test Method | DUPONT USA/73G30L NC010 |
|---|---|---|---|
| Odor | VDA270 | 3.50 | |
| Emissions of Organic Compounds | VDA277 | 8.50 µgC/g |
| Electrical performance | Test Condition | Test Method | DUPONT USA/73G30L NC010 |
|---|---|---|---|
| Compared to the Leakage Tracking Index (CTI) | IEC 60112 | PLC 0 | |
| Volume resistivity | IEC 60093 | 1E+14 ohms·cm | |
| relative permittivity | 100Hz | IEC 60250 | 3.80 |
| Dissipation Factor | 100Hz | IEC 60250 | 0.022 |
| Compared to the Leakage Tracking Index (CTI) | CTI | UL 746 | PLC 0 |
| Mechanical properties | Test Condition | Test Method | DUPONT USA/73G30L NC010 |
|---|---|---|---|
| Tensile modulus | ISO 527-2 | 10000 Mpa | |
| Tensile creep modulus | 1hr | ISO 899-1 | -- Mpa |
| compression stress | ISO 604 | 160 Mpa | |
| Flexural modulus | ASTM D790/ISO 178 | 9000 kg/cm²(MPa)[Lb/in²] | |
| bending strength | ISO 178 | 240 Mpa | |
| Tensile strain | 断裂 | ISO 527-2 | 3.5 % |
| Flexural modulus | ISO 178 | 8500 Mpa | |
| Tensile creep modulus | 1000hr | ISO 899-1 | -- Mpa |
| tensile strength | 断裂 | ISO 527-2 | 180 Mpa |
| Tensile modulus | ASTM D638/ISO 527 | 9100 kg/cm²(MPa)[Lb/in²] | |
| shear strength | ASTM D732 | 60.0 Mpa | |
| Charpy Notched Impact Strength | ASTM D256/ISO 179 | 6 kg·cm/cm(J/M)ft·lb/in |
| Physical properties | Test Condition | Test Method | DUPONT USA/73G30L NC010 |
|---|---|---|---|
| Water absorption rate | ASTM D570/ISO 62 | 1.8 % |
| flammability | Test Condition | Test Method | DUPONT USA/73G30L NC010 |
|---|---|---|---|
| UL flame retardant rating | 3.0mm | IEC 60695-11-10,-20 | HB |
| 3.0mm | UL 94 | HB | |
| 1.5mm | IEC 60695-11-10,-20 | HB | |
| FMVSS flammability | FMVSS302 | B | |
| atomization | F-value(refraction) | ISO 6452 | 95 % |
| G-value(condensate) | ISO 6452 | 1E-04 g | |
| UL flame retardant rating | 1.5mm | UL 94 | HB |
| Limiting Oxygen Index | ISO 4589-2 | 21 % | |
| burning rate | 1.00mm | ISO 3795 | 25 mm/min |
| physical property | Test Condition | Test Method | DUPONT USA/73G30L NC010 |
|---|---|---|---|
| Shrinkage rate | TD | ISO 294-4 | 0.60 % |
| MD | ISO 294-4 | 0.20 % | |
| Water absorption rate | 饱和,23°C,2.00mm | ISO 62 | 6.3 % |
| 平衡,23°C,2.00mm,50%RH | ISO 62 | 1.9 % |
| Thermal performance | Test Condition | Test Method | DUPONT USA/73G30L NC010 |
|---|---|---|---|
| melting temperature | ISO 11357-3 | 221 °C | |
| Heat distortion temperature | HDT | ASTM D648/ISO 75 | 210 ℃（℉） |
| vicat | ASTM D1525/ISO R306 | 215 ℃（℉） | |
| Heat distortion temperature | 0.45MPa,未退火，HDT | ISO 75-2/B | 220 °C |
| 1.8MPa,未退火，HDT | ISO 75-2/A | 210 °C | |
| Linear coefficient of thermal expansion | MD | ISO 11359-2 | 1.4E-05 cm/cm/°C |
| melting temperature | 221 ℃（℉） | ||
| Linear coefficient of thermal expansion | TD | ISO 11359-2 | 1E-04 cm/cm/°C |
| Glass Transition Temperature | ISO 11357-2 | 60.0 °C |